分别在室温和基片温度低于223 K的条件下,采用直流反应磁控溅射法制备WO3薄膜.对两种条件下制备的薄膜晶体结构、透射光谱特性及电致变色性能进行对比分析.结果表明,低温沉积有利于WO3薄膜非晶化,使得Li+的抽取更加容易,进而显示出良好的变色性能.低温制备的WO3薄膜在可见光400～800 nm范围内着色态和漂白态平均透光率差值达70%以上,在690 nm处的着色系数达到了48.7 cm2/C,具有良好的变色效率.
参考文献
| [1] | Washizu E.;Yamamoto A.;Abe Y.;Kawamura M.;Sasaki K. .Optical and electrochromic properties of RF reactively sputtered WO3 filMS[J].Solid state ionics,2003(1/4):175-180. |
| [2] | Z.Dimitrova;D.Gogova .On the structure,stress and optical properties of CVD tungsten oxide films[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2005(2):333-340. |
| [3] | 叶辉,李晓艳.溶胶-凝胶法制备电致变色薄膜及器件的研究[J].光学学报,1999(04):532-539. |
| [4] | Fanghan B W et al.[J].R C S Rev,1975,36:177. |
| [5] | 王丽阁,胡远荣,李国卿,谢为.中频孪生磁控溅射WO3薄膜及变色性能研究[J].光学学报,2006(06):938-942. |
| [6] | G.A.de Sijs;R.A.de Groot .Amorphous WO_3: a first -principles approach[J].Electrochimica Acta,2001(13/14):1989-1993. |
| [7] | 唐伟忠.薄膜材料制备原理、技术及应用[M].北京:冶金工业出版社,1999:121. |
| [8] | 孙艳,马珩,段潜,陈静,戴宁.溶胶-凝胶法制备三氧化钼电致变色薄膜的研究[J].光学仪器,2004(02):128-131. |
| [9] | Lin-Chi Chen;Kuo-Chuan Ho .Design equations for complementary electrochromic devices:application to the tungsten oxide-Prussian blue system[J].Electrochimica Acta,2001(13/14):2151-2158. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%