针对5 mm厚航空用铝合金7050-T7451进行了不同焊速时搅拌摩擦焊接头的微观结构和低周疲劳性能的研究.结果表明:接头焊核区面积与焊核区晶粒度都随着焊接速度的增加而减小;转速为400 r/min、焊速为40 mm/min时,接头具有最好的疲劳性能;搅拌摩擦焊接头的低周疲劳裂纹均在接头底部启裂,沿前进侧热机械影响区与焊核区的过渡区域扩展至断裂.
参考文献
| [1] | Rhodes C G;Mahoney M W;Flintoff J G et al.Effect of friction stir welding on microstructure of 7075 aluminum[J].Scripta Materialia,1997,36(01):69-71. |
| [2] | A. Squillace;A. De Fenzo;G. Giorleo .A comparison between FSW and TIG welding techniques: modifications of microstructure and pitting corrosion resistance in AA 2024-T3 butt joints[J].Journal of Materials Processing Technology,2004(1):97-105. |
| [3] | Rollin M;Collins E.The use of frietion welding technology in maritine application A[A].Indianapolis,America:TMS,2001:189-195. |
| [4] | M. Ericsson;R. Sandstrom .Influence of welding speed on the fatigue of friction stir welds, and comparison with MIG and TIG[J].International Journal of Fatigue,2003(12):1379-1387. |
| [5] | Zhou CZ;Yang XQ;Luan GH .Effect of oxide array on the fatigue property of friction stir welds[J].Scripta materialia,2006(8):1515-1520. |
| [6] | Diekerson T L;Przydatek J .Fatigue of friction stir welds in ahminium alloys that contain root flaws[J].International Journal of Fatigue,2003,25:1399-1409. |
| [7] | Cavaliere P et al.Effect of welding parameters on mechanical and microstruetural properties of AA6056 joints produced by friction stir welding[J].Journal of Materials Processing Technology,2006,180:263-270. |
| [8] | 徐灏.疲劳强度[M].北京:高等教育出版社,1988:226-233. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%