研制了一种以磷酸、磷酸盐、硼化物等为原材料的磷酸盐涂料,在不同温度下烧结处理后,对其抗氧化性能及表面微观形貌进行研究.结果表明:650℃烧结的涂层氧化防护性能明显优于900℃烧结的;在700℃氧化30 h后,最小氧化失重率仅为1.76%,氧化后涂层仍然保持完整致密;经过900℃、3 min<=>室温、2min循环30次和l 100℃、3 min<=>室温、2 min循环10次的连续热震后,失重率为1.97%,涂层与C/C基体结合良好,涂层的热性能稳定.
参考文献
| [1] | 王茂章;贺福.碳纤维及其复合材料[M].北京:科学出版社,1997:271-361. |
| [2] | Savage G.Carbon-carbon composite[M].London:Chapman＆ Hall Press,1993:323-360. |
| [3] | Donald L.Schmidt Kenneth E.David .Unique application of carbon-carbon composite materials(1)[J].SAMPE Journal,1999(3):27-39. |
| [4] | Schmidt DL;Theibert LS;Davidson KE .Unique applications of carbon-carbon composite materials. II[J].SAMPE Journal,1999(4):51-63. |
| [5] | Schmidt DL;Theibert LS;Davidson KE .Unique applications of carbon-carbon composite materials. III[J].SAMPE Journal,1999(5):47-55. |
| [6] | Bacos MP.;Lavigne O.;Renollet Y.;Dorvaux JM. .C/C composite oxidation model I. Morphological experimental investigations[J].Carbon: An International Journal Sponsored by the American Carbon Society,2000(1):77-92. |
| [7] | 李贺军.炭/炭复合材料[J].新型炭材料,2001(02):79-80. |
| [8] | 杨尊社,卢刚认,曲德全,楼建军,赵文庆,潘亚萍.C/C复合材料的磷酸盐与硼系涂料的防氧化研究[J].材料保护,2001(03):12-13. |
| [9] | 彭志刚;肖志超;苏君明 等.防止碳/碳复合材料氧化的方法[P].中国专利 CN1544827A |
| [10] | Wang Q .Effect of boron on graphite oxidation-A theoretical study[J].CARBON,1997,35:307-313. |
| [11] | 薛宁娟;肖志超;苏君明 等.飞机碳/碳刹车盘用防氧化涂层及其制备方法[P].中国专利,CN101 153123 |
| [12] | 葛毅成,易茂中,李丽娅,黄伯云.含P,B,Si化合物涂层对C/C复合材料抗氧化性能的影响[J].粉末冶金材料科学与工程,2003(03):260-264. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%