利用超声速平板试验技术,对两种低密度烧蚀材料在高焓、低热流(气流剪切力70 N/m~2,冷壁热流密度200 kW/m~2,气流总焓12 MJ/kg,压力1 kPa,试验时间300 s)条件下进行了高温气动剪切试验.试验中通过试验件的不同安装方式,综合考核了材料的性能及工艺.结果表明:两种低密度烧蚀材料试验过程中无明显剥蚀,表面碳层完整,材料的抗剪切性能较好,两种材料表面烧蚀较为均匀,材料间的粘接缝没有明显的开裂,也没有出现冲刷凹槽,材料的热匹配性能较好;材料与底板之间没有脱落现象,粘接工艺较好.
Shear tests on low density ablation materials were carried out by using the flat panel models on supersonic arc jet stream. The surface shear stresses, the cold wall heat flux, the total enthalpy, the surface pressure and the test time were 70 N/m~2 ,200 kW/m~2, 12 MJ/kg, 1 kPa and 300 s respectively. The performances and technology of two kinds of low density ablation materials were checked by different installation of models in test. The materials have no erosion and the char remained intact. The surface recessions are almost the same and the filled gap between materials are well. The materials are not separated from the back plate. The results show that materials possess good performances of anti-shear, thermal matching and good sticking.
参考文献
| [1] | 赵梦熊.载人飞船空气动力学[M].北京:国防工业出版社,2000:97-110. |
| [2] | Tauber Michael;Tran Huy .Ames research center shear tests of SLA -561V heat shield material for mars-pathfinder[NASA-TM-110402][R].,1996. |
| [3] | 张友华,刘德英,杨汝森,杨国铭,刘燕松.涂层材料长时间气动加热实验研究[J].宇航材料工艺,2007(04):70-72. |
| [4] | 张友华,董永晖,陈连忠.大尺度空气舵超声速烧蚀热结构试验[J].宇航材料工艺,2008(05):78-80. |
| [5] | 张志成.高超声速气动热和热防护[M].北京:国防工业出版社,2003:278-281. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%