用两步化学氧化法在铝合金表面获得了黑色氧化膜.利用全浸渍腐蚀试验及电化学极化曲线评价了膜的耐蚀性能,利用扫描电子显微镜观察膜的表面形貌,采用能量散射谱(EDS)测定膜的成分.结果表明:铝合金的黑色氧化膜具有网块状结构,膜层主要由O、Al、Mn、Co、Cr五种元素所组成,未经封闭的铝合金氧化膜的耐蚀性能很差,而经重铬酸钾封闭后,耐蚀性大为提高.
Black oxidation film was obtained on Aluminium Alloy by two-step oxidation. The anticorrosion prop-erties of the film were evaluated by neutral salt spray tests and electrochemical polarization curve. The morphology of the film was studied by scanning electron microscope. The composition of oxidation film was determined by EDS. This experiment result indicated that the oxidation film coatings had large lumps with lots of crackles by SEM experiments and that the oxidation film consisted of oxygen, aluminum, manganese, cobalt and chromium and that the treated Al without sealing had a lower corrosion resistance in 3.5% NaCl solution, but the samples sealed by K_2Cr_2O_7 has a good corrosion resistance in 3.5% NaCl solution.
参考文献
| [1] | 郭红霞.铝及铝合金着色工艺[J].表面技术,2004(01):59-60. |
| [2] | 熊老伍.铝合金亮黑色涂层工艺[J].电镀与精饰,2004(04):23-24. |
| [3] | 郝建军,牟世辉,赵平,孟晓毅.铝合金阳极氧化着黑色工艺的研究[J].沈阳工业学院学报,1999(03):36-40. |
| [4] | 华树芳.压铸铝合金枪黑色电镀工艺[J].电镀与涂饰,2003(03):11-13. |
| [5] | 旷亚非,许岩,李国希.铝及其合金材料表面处理研究进展[J].电镀与精饰,2000(01):16-20. |
| [6] | 邓立元,钟宏,杨余芳,周书天.铝合金化学发黑新工艺[J].电镀与涂饰,2004(02):16-18. |
| [7] | 张金涛,潘亮,李春东.LY12铝合金表面硅烷杂化膜的电化学性能研究[J].电镀与涂饰,2008(09):22-25. |
| [8] | 王成,江峰.LY12Al合金铬磷化处理[J].腐蚀科学与防护技术,2002(02):82-85. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%