针对新型航天飞行器高温隔热(约1 500℃)的迫切需求,开展了超高温刚性隔热材料的制备和性能研究.采用陶瓷纤维和无机粘结剂,经过湿法抽滤成型、高温热处理等工艺制备了刚性隔热材料.对材料的微观结构、热物理和力学性能进行了表征、测试.结果表明:纤维有效粘结在一起；通过改变纤维和粘结剂的比例,可以调节材料性能；热导率、力学性能与密度近似呈直线关系.材料在1 500℃经1h处理后线收缩率＜2％,密度为0.3～0.5 g/cm3,热导率为0.06～0.09 W/(m·K),压缩强度为0.6～1.2 MPa.
参考文献
| [1] | Cleland J;Iannetti F .Thermal protection system of the space shuttle[NASA contractor report 4227][R].,1989. |
| [2] | Hank J M;Murphy J C;Mutzman R C .The X-51A scramjet engine flight demonstration program[MAA 2008-2540][R]. |
| [3] | 李俊宁,胡子君,孙陈诚,吴文军,张宏波.高超声速飞行器隔热材料技术研究进展[J].宇航材料工艺,2011(06):10-13,31. |
| [4] | Banas R P;Creedon J F;Cunnington G R .Thermophysical and mechanical properties of the HTP family of rigid ceramic insulation materials[AIAA-85-1055][R]. |
| [5] | Barney A O;Heng V;Oka K S .Hybrid aerogel rigid ceramic fiber insulation and method of producing same[P].US Patent,6770584,2004. |
| [6] | 孙陈诚;胡子君;李俊宁 等.一种轻质刚性陶瓷隔热瓦及其制备方法[P].中国专利,CN102199042A |
| [7] | 赵小波;魏美玲;刘瑞祥 等.石英纤维复合隔热材料及其制备方法[P].中国专利,CN101659557A,2010. |
| [8] | 王钦,胡子君,孙陈诚,鲁胜,李俊宁.陶瓷隔热瓦力学性能影响因素及其稳定性控制[J].宇航材料工艺,2010(02):77-79. |
| [9] | Speil S .Low density thermal insulations for aerospace applications[J].Appl Mater Res,1964,3(04):238-242. |
| [10] | [OL].http://www.zircarceramics.com |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%