以硝酸氧锆为锆源,尿素为凝胶促进剂,通过水热凝胶法结合超临界乙醇干燥,可成功制备出具有良好纳米三维网络结构的ZrO2气凝胶.采用透射电镜(TEM)、比表面积及孔隙度分析仪(BET),X射线衍射仪等测试手段对其结构进行了表征与测试.结果表明,ZrO2气凝胶主要由无定型和四方晶相组成,其比表面积为445 m2/g,孔径主要分布在5～7 nm和30～40 nm两处.
参考文献
| [1] | 李映伟,贺德华,袁余斌,程振兴,朱起明.纳米二氧化锆催化剂上一氧化碳加氢合成异丁烯[J].催化学报,2002(02):185-190. |
| [2] | Su Caili. .Synthesis of isobutene from synthesis gas over nanosize zirconia catalysts[J].Applied Catalysis, A. General: An International Journal Devoted to Catalytic Science and Its Applications,2000(1):81-89. |
| [3] | Hertz Audrey;Corre Yves-Marie .Yttria stabilized zirconia synthesis in supercritical CO2:understanding of particle formation mechanisms in CO/co-solvent systems[J].Journal of the European Ceramic Society,2010,30:1691-1698. |
| [4] | Ren .Copper and Silver-Zirconia aerogels:preparation,structural properties and catalytic behavior in methanol synthesis from carbon dioxid[J].Journal of Catalysis,1998,179:515-527. |
| [5] | 张蓉艳;金承黎 .一种水热合成低成本快速制备气凝胶的方法[P].CN 101456569A,2008-07-22. |
| [6] | 程虎民,马玉荣,廖复辉,马季铭,齐利民.水热均匀沉淀法合成中孔氧化锆[J].物理化学学报,2003(04):326-328. |
| [7] | Clearfield A .Structural aspects of zirconium chemistry[J].Rev Pure Appl Chem,1964,14:91-108. |
| [8] | 梁丽萍,侯相林,吴东.超临界CO2流体干燥合成ZrO2气凝胶及其表征[J].材料科学与工艺,2005(05):552-555. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%