通过常规力学性能、扫描电镜、透射电镜等测试分析方法研究了T8I6二次时效制度对Mg、Ag和Zn复合微合金化的Al-3.48Cu-1.44Li合金微观组织和力学性能的影响.结果表明,与单级时效相比,二次时效合金强度提高,而塑性略降;合金强度随第三级时效时间的延长进一步提高.最优的合金其抗拉强度(UTS)、屈服强度(YS)和延伸率分别为613.7、564.9 MPa和6.8％.合金的强化相主要为T1相,另有少量的θ'相和S'相.二次时效促进强化相,特别是T1相的二次沉淀,提高合金的强度,同时几乎不损失塑性.
参考文献
| [1] | Lavernia E J;Srivatsan T S;Mohamed F A et al.Review Strength,deformation,fracture behaviour and ductility of aluminium-lithium alloys[J].Journal of Materials Science,1990,25:1137-1158. |
| [2] | Brandon Bodily;Markus Heinimann;Gary Bray.Advanced Aluminum solutions for next-gen aerospace structures[J].AEROSPACE ENGINEERING,2013(02):34-37. |
| [3] | 袁志山,陆政,谢优华,戴圣龙,刘常升.高强Al-Cu-Li-X铝锂合金2A97三级时效工艺及性能研究[J].航空材料学报,2006(03):79-82. |
| [4] | R. N. Lumley;I. J. Polmear;A. J Morton .Interrupted aging and secondary precipitation in aluminium alloys[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2003(11):1483-1490. |
| [5] | 孙刚,王少华,马志峰,陆政,冯朝辉,张显峰.新型Al-Zn-Mg-Cu合金型材二次时效处理后的组织与性能[J].金属热处理,2012(09):51-55. |
| [6] | 于利军,郑子樵,李世晨,刘岗,魏修宇.热处理工艺T6I6对2195合金组织和性能的影响[J].材料热处理学报,2006(05):79-83. |
| [7] | Romios M;Tiraschi R;Parrish C et al.Design of multistep aging treatments of 2099 (C458) Al-Li alloy[J].Journal of Materials Engineering and Performance,2005,14(05):641-646. |
| [8] | Kumar K S;Heubaum F H .The effect of Li content on the natural aging response of Al-Cu-Li-Mg-Ag-Zr alloys[J].Acta Materialia,1997,45:2317-2327. |
| [9] | Nie J F;Muddle B C .Effect of precipitate shape and orientation on dispersion strengthening in high strength Aluminum alloys[J].Materials Science Forum,1996,217-222:1257-1262. |
| [10] | B. Decreus;A. Deschamps;F. De Geuser .The influence of Cu/Li ratio on precipitation in Al-Cu-Li-x alloys[J].Acta materialia,2013(6):2207-2218. |
| [11] | 张坤,戴圣龙,黄敏,杨守杰,颜鸣皋.高纯Al-Cu-Mg-Ag合金的多级断续时效工艺研究[J].航空材料学报,2007(04):1-5. |
| [12] | 李海,郑子樵,王芝秀.7055铝合金二次时效特征研究-（Ⅰ）力学性能[J].稀有金属材料与工程,2005(07):1029-1032. |
| [13] | R. N. Lumley;I. J. Polmear;A. J. Morton .Development of mechanical properties during secondary aging in aluminium alloys[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2005(9):1025-1032. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%