通过电偶腐蚀、加速腐蚀和缝隙腐蚀试验,研究了液体推进剂贮箱材料的电化学腐蚀行为,并用光学显微镜观察了试验后的材料表面腐蚀形貌.结果表明,铝合金LF6、LD10、2219和LF3与不锈钢1Cr18 Ni9Ti和316L的电偶电流均小于0.3 A/cm2,属于A级相容;无论贮箱箱体主材料为LD10或2219,在与箱体附件材料LF3组成的电偶对中,LD10和2219均为阴极金属受到保护;2219和LD10在20℃室温、68%硝酸环境下的阳极极化曲线相似,年腐蚀速率相当.

参考文献

[1] Juzeliunas E;Sudavicius A;Juttner K.Study of initial stages of Al-Mg alloy corrosion in water,chloride and Cu (Ⅱ) environment by a scanning Kelvin probe and XPS[J].Electrochemistry Communications,2003(05):154-158.
[2] J. H. W. de Wit .Local potential measurements with the SKPFM on aluminium alloys[J].Electrochimica Acta,2004(17/18):2841-2850.
[3] Monica T;Stefano P T .Study of Al alloy corrosion in neutral NaCl by the pitting scan technique[J].Mater Chem Phys,2010,121:523.
[4] Zaki Ahmad;Anwar Ul-Hamid;Abdul-Aleem B. J. .The corrosion behavior of scandium alloyed Al 5052 in neutral sodium chloride solution[J].Corrosion Science,2001(7):1227-1243.
[5] 汪俊英,孔小东,刘信.铝合金在NaCl溶液中的电化学腐蚀行为[J].装备环境工程,2010(03):38-41.
[6] 杨萍,黎学明,宗庆彬,邱妮,姚强,苗玉龙.电力系统用LF21铝合金的电化学腐蚀行为[J].腐蚀科学与防护技术,2012(04):309-313.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%