采用Pechini溶胶-凝胶法制备出了适于电子墨水用的实心球形TiO2白色显色颗粒,颗粒粒度约为300 nm.采用热重-差热、X射线衍射、扫描电子显微镜等分析方法,研究了前驱物的组成对所得颗粒的形貌、粒径和分散程度的影响规律以及TiO2颗粒的晶相转变温度.研究表明:络合物经过煅烧,在500 ℃时开始出现锐钛矿相TiO2,800 ℃时由锐钛矿相向金红石相转变;不同条件下制备的TiO2均为球形颗粒,TiO2颗粒的粒径随Ti(SO4)2浓度的增大而增大,当柠檬酸的质量分数为12 %时,TiO2颗粒的粒径有最小值.
参考文献
| [1] | Rong Yu,Chen Hong-zheng,Li Han-ying,et al.Encapsulation of titanium dioxide particles by polystyrene via radical polymerization[J].Colloids and Surfaces A:Physicochem.Eng.Aspects,2005,253(1-3),193-197. |
| [2] | 段晓霞,徐征,滕枫,等.基于电泳技术的电子纸研究进展[J].液晶与显示,2004,19 (5):380-385. |
| [3] | Jacobson Joseph M,Drzaic Paul S,Morrison Ian D.Electronicphoretic displays using nanoparticles:US,6323989[P].2001-11-27. |
| [4] | 郭慧林,王允韬,刘曙.电子墨水的组成及制备方法[J].功能材料,2003,34(4):386-389. |
| [5] | Robert A H,Feenstra B J.Video-speed electronic paper based on electrowetting[J].Nature,2003,425(6956):383-385. |
| [6] | 王建平,赵晓鹏.蓝色电子墨水微胶囊的制备及其电场响应行为[J].液晶与显示,2004,19(6):434-439. |
| [7] | Schubert H.Suspension for use in electrophoretic image display systems:US,5380362[P].1995-01-10. |
| [8] | 刘付胜聪,肖汉宁,李玉平,等.纳米TiO2表面吸附聚乙二醇及其分散稳定性的研究[J].无机材料学报,2005,20(2):310-316. |
| [9] | 邓捷,吴立峰.钛白粉应用手册[M].修订版.北京:化学工业出版社,2004:23-24. |
| [10] | Guo Hai,Yin Min,Dong Ning,et al.Effect of heat-treatment temperature on the luminescent properties of Lu2O3∶Eu film prepared by Pechini sol-gel method[J].Appl.Surf.Sci.,2005,243(1-4):247-252. |
| [11] | 逄茂林,林君,程子泳,等.Y2O3∶Eu3+发光薄膜的溶胶-凝胶法制备、表征及图案化[J].中国稀土学报,2002,20(6):544-547. |
| [12] | Dhagea S R,Renu Pasrichab,Ravi V.Synthesis of ultrafine TiO2 by citrate gel method[J].Mater.Res.Bulletin,2003,38(11-12):1623-1628. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%