用CVD方法在钨丝和碳纤维上沉积金刚石薄膜。约含有10000根纤维的纤维束经特殊 处理后分离为单根。生长条件使碳纤维中心在CVD生长结束后仍保持固态。CVD金刚石在纤 维上生长的平均激活能为93.15kJ/mol。SEM照片给出了纤维涂层在不同生长条件下的表面和 中心的形貌。纤维内部的石墨碳和外部的金刚石层有很大的不同。钨丝的断裂强度和杨氏模量 的测量表明，具有金刚石涂层的钨丝的断裂强度为0.567GPa，非常接近不具有金刚石涂层的钨 丝的断裂强度。但具有金刚石涂层的钨丝的断裂应变为4.8％，比没有金刚石涂层的钨丝的断 裂应变7％要小得多。这表明了金刚石涂层可以减少钨丝的断裂应力，提高其机械性能。
Diamond growth on W－wire and C－fiber substrates was studied. A treatment was used to separate fibers one by one from a bunch of more than 10000 fibers. The selected growth condition was to keep the carbon fiber core solid after CVD growth. Activation energy of CVD coated fibers is 93.15 kJ/mol in average. SEM pictures show surface and core morphology of the coatings under different treatment conditions. There are two different contrasts related to interior graphite carbon and exterior diamond layer. Wire fracture strength and Young's modulus measurement indicates that the fracture strength of W wire with diamond coating is 0.567 GPa, very close to its value without coating. However, the fracture strain of the wire with diamond coating is 4.8％ , which is much less than that of W wire fracture strain of 7％ . It means that diamond coated wire may reduce wire fracture strain and improve its mechanical property.
参考文献
| [1] | LUGSCHEIDER E;MULLER U .Evaluation of d c - plasma jet chemical vapour deposition for diamond coatings on tungsten carbide based cutting plates[J].Diamond and Related Materials,1993,2:1464. |
| [2] | Ubhi HS.;Partridge PG.;Williamson NJ.;Gilmore CJ. .Microstructure of the interface between chemical vapour-deposited diamond and platinum substrate[J].Journal of Materials Science,1998(15):3785-3789. |
| [3] | GRIFFITH P W;WISBEY A;WOOD M J et al.Microstructure and tensile properties of continuous diamond fiber reinforced titanium alloy[J].Diamond and Related Materials,1998,7:957. |
| [4] | Lu G H;PARREIDGE P G .A technique for the manufacture of long hollow diamond chemical vapour deposition[J].Journal of Materials Science Letters,1995,14:1448. |
| [5] | WIELAGE BERNBARD;DORNER ANNETT.Bonding and sliding wear behavior of diamond- like carbon coatings on fiber reinforced aluminum[A].Switzerland:Elsevier Science,1998 |
| [6] | MAY W;REGO C A;Thomas R M et al.Preparation of solid and hollow diamond fibers and the potential for diamond fibre metal matrix composites[J].Journal of Materials Science Letters,1994,13:247. |
| [7] | Partridge PG;Nabiyouni G;Schwarzacher W;Nicholson JA;Nicholson ED;Bleay S;Gilmore C .Magnetic diamond fibres[J].Materials Science and Technology: MST: A publication of the Institute of Metals,1997(6):453-458. |
| [8] | KONDCH E;OHTA T .Determination of activition energies for diamond growth by an advanced hot filament chemical vapor deposition method[J].Applied Physics Letters,1991,59:488. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%