采用XRD、SEM、IR光谱和物理测试等方法,研究了碳纳米粉的结构与性能及电化学性能.结果表明碳纳米粉的粒度为30nm, 具有石墨结构;碳纳米粉的首次放电比容量为391.5mAh/g,首次循环可逆比容量是336.0 mAh/g,不可逆容量仅是21.9 mAh/g.碳纳米粉的循环伏安曲线的峰形与峰位基本相同,没有还原电流峰.结果显示碳纳米粉适用于做锂离子电池负极材料.
参考文献
[1] | 杨晓西,王铁军,丁静,杨建平.锂离子电池及其材料的发展近况[J].华南理工大学学报,1999(05):52. |
[2] | 黄振谦 .锂离子电池负极材料的研究[J].电池,1998,28(02):51-59. |
[3] | MANEV V .Electrochemical performance of nature brazilian graphite as anode material for Lithium-ion rechargeable cells[J].Journal of Power Sources,1995,55:211-215. |
[4] | 吴升晖 .锂离子电池负极材料的研究[J].电源技术,1998,22(01):35-39. |
[5] | Iijima S .Helical Microtubules of Griphitic Carbon[J].Nature,1991,354:56. |
[6] | Ebbesen T W;Ajayan P M .Large-scale sythesis of carbon nanotube[J].Nature,1992,358:220. |
[7] | Ding R G;Lu G Q;Yang Z F et al.Recent advances in the preparation and utilization of carbon nanotubes for hydrogen storage[J].Journal of NANOSCIENCE AND NANOTECHNOLOGY,2001,1:7-29. |
[8] | Kazunori Anazawa;Kei Shimotani;Chikara Manabe;Hiroyuki Watanabe;Masaaki Shimizu .High-purity carbon nanotubes synthesis method by an arc discharging in magnetic field[J].Applied physics letters,2002(4):739-741. |
[9] | LEE S J;Baik H K;Yoo J et al.Large scale synthesis of carbon nanotubes by plasma arc discharge technique[J].Diamond and Related Materials,2002,11(3-6):914-917. |
[10] | Huang H J;Marie J;Kajiura M et al.Improved oxidation resistance of single-walled carbon nanotubes produced by arc discharge in a bowl-bike cathode[J].NANO LETTERS,2002,2:1117. |
[11] | Liu C;Cong H T;Li F et al.Semi-continuous synthesis of single-walled carbon nantoubes by a hydrogen arc discharge method[J].Carbon,1999,37:1865-1868. |
[12] | Hemadi K;Fonseca A;Nagy J B et al.Production of nanotubes by the catalytic decomposition of different carbon-containing compounds[J].Applied Catalysis A:General,2000,199:245. |
[13] | 李新海,杨占红,陈志国,王红强,李添宝,沈宁一,李晶.炭纳米管的提纯-重铬酸钾氧化法[J].新型炭材料,1999(03):32-36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%