本文介绍模压法成形制备TiH2粉及TiH2-6Al-4V合金粉压坯,探讨粉末的成形性及压坯密度随压力的变化.在不添加成形剂的情况下,采用模压法制备成形坯,试验发现粗TiH2(40μm)粉末容易成形,球磨30min TiH2粉末难成形,成形后容易出现裂纹,且球磨时间越长成形就越困难.粗TiH2粉末(40μm)、高能球磨30min TiH2粉末和TiH2-6Al-4V粉末的压坯密度都随压力的增大而增大.在相同的压制压力下,粗TiH2粉末(40μm)的压坯密度比高能球磨30minTiH2粉末的压坯密度高.
参考文献
| [1] | 莫畏.钛[M].北京:冶金工业出版社,2008:4. |
| [2] | 赵嘉琪,南海,黄东.氢合金化钛合金粉末成形制件技术的发展[J].特种铸造及有色合金,2007(08):593-595. |
| [3] | 喻岚,李益民,邓忠勇,李笃信.粉末冶金钛合金的制备[J].轻金属,2003(09):43-47. |
| [4] | Rack HJ;Qazi JI .Titanium alloys for biomedical applications[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2006(8):1269-1277. |
| [5] | Vinicius A. R. Henriques;Cesar E. Bellinati;Cosme R. M. da Silva .Production of Ti-6%Al-7%Nb alloy by powder metallurgy (P/M)[J].Journal of Materials Processing Technology,2001(1/3):212-215. |
| [6] | 王桂生;田荣璋.钛的应用技术[M].长沙:中南大学出版社,2007:401. |
| [7] | FROES F H;EYLON D.Titanium Net Shape Technologies[M].Los Angeles:The Metallurgical Society of AIME Press,1984:1-20. |
| [8] | EYLON D;FROES F H;PARSONS L D .Titanium PM components for advanced aerospace application[J].Metal Powder Report,1983,38(10):567-571. |
| [9] | 焦明华,柏厚义,俞建卫,宋平,解挺.金属粉末压制成形的细观模拟研究[J].金属功能材料,2008(05):28-32. |
| [10] | MERHAR J R .Overview of Metal Injection Moulding[J].Metal Powder Report,1990,45(05):339-342. |
| [11] | D. H. Abbott .AeroMet implementing novel Ti process[J].Metal Powder Report,1998(2):24-26. |
| [12] | KEICHER D M;SMUGERESKY J E .The laser forming of metallic components using particulate materials[J].Journal of the Minerals Metals & Materials Society,1997,49(05):51-54. |
| [13] | 陈振华.现代粉末冶金技术[M].北京:化学工业出版社,2007:284. |
| [14] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,2004:173. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%