聚二甲基硅氧烷(PDMS)的表面改性与键合是微流控芯片制作中的关键技术之一.本文比较分析了PDMS常用表面改性方法的优缺点,利用电晕放电仪在常温环境下产生的氧等离子体实现了对PDMS表面改性及不可逆键合,优化了电晕放电仪的表面处理参数,重点测试了PDMS分别与PDMS和PMMA之间的键合强度.并与紫外照射、表面活化剂等表面改性方法得到的键合进行了强度比较.键合强度测试结果表明:常温下氧等离子体表面改性效果略逊于真空环境中的氧等离子体表面处理,但是其键合强度达到700KPa,高于其它表面改性方法的键合强度.
参考文献
[1] | George M .Whitesides.the origins and the future of microfluidics[J].Nature,2006,442:368-373. |
[2] | Jessamine M.K.Ng;Irina Gitlin;Abraham D. Stroock;George M.Whitesides .Components for integrated poly (dimethylsiloxane) microfluidic systems[J].Electrophoresis,2002,23:3461-3473. |
[3] | George M.Whitesides;Abraham D.Stroock.Flexible methods for microfluidics[J].Physics Today,2001:42-48. |
[4] | Hillborg H.;Gedde UW.;Smith GD.;Yasuda HK.;Wikstrom K.;Ankner JF. .Crosslinked polydimethylsiloxane exposed to oxygen plasma studied by neutron reflectometry and other surface specific techniques[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(18):6851-6863. |
[5] | Shantanu Bhattacharya .Plasma bonding of poly (dimethyl) siloxane and glass surfaces and its application to microfluidics[D].Texas in USA:Texas Tech University,2003. |
[6] | Mark A Eddings;Michael A Johnson;Bruce K Gale.Determing the optical PDMS-PDMS bonding technique for microfluidic devices[J].J Mciromech Microeng,2008:18. |
[7] | Bhattacharyya A;Klapperich CM .Mechanical and chemical analysis of plasma and ultraviolet-ozone surface treatments for thermal bonding of polymeric microfluidic devices[J].Lab on a chip,2007(7):876-882. |
[8] | S Schlautmann;G A J Besselink;Radhakrishna Prabhu G;R B M Schasfoort .Fabrication of a microfluidic chip by UV bonding at room temperature for integration of temperature-sensitive layers[J].Journal of Micromechanics and Microengineering,2003,13:81-84. |
[9] | Jeonggi Seo;Luke P .Lee,Effects on wettability by surfactant accumulation/depletion in bulk polydimethylsiloxane (PDMS)[J].Sensors and Actuators B:Chemical,2006,119:192-198. |
[10] | Seunghwan Lee;Janos Voros .An Aqueous-Based Surface Modification of poly(dimethylsiloxane)with poly(ethylene glycol)to Prevent Biofouling[J].Langmuir: The ACS Journal of Surfaces and Colloids,2005(25):11957-11962. |
[11] | Ginn B.T;Steinbock O .Polymer surface modification using microwave-oven-generated plasma[J].Langmuir,2003,19:8117-8118. |
[12] | Haubert K;Drier T;Beebe D .PDMS bonding by means of a portable, low-cost corona system[J].Lab on a chip,2006(12):1548-1549. |
[13] | Shantanu Bhattacharya;Arindom Datta;Jordan M. Berg;Shubhra Gangopadhyay .Studies on Surface Wettability of Poly(Dimethyl) Siloxane (PDMS) and Glass Under Oxygen-Plasma Treatment and Correlation With Bond Strength[J].Journal of Microelectromechanical Systems: A Joint IEEE and ASME Publication on Microstructures, Microactuators, Microsensors, and Microsystems,2005(3):590-597. |
[14] | 刘晓为;王蔚;田丽;宣雷 鲍志勇 .一种以聚二甲基硅氧烷为基材的简易不可逆键合方法[P].中国专利:1683443A,2005-10-19. |
[15] | Xiaohui Lin;Guanglan Liao;Zirong Tang;Tielin Shi .UV surface exposure for low temperature hydrophilic silicon direct bonding[J].Microsystem technologies,2009(2):317-321. |
[16] | His Yin Tan;Weng Keong Loke;Nam-Trung Nguyen.Integration of PDMS and PMMA for batch fabrication of microfluidic devices[A].,2010:1177-1118. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%