选用日本东邦THA-3K型炭纤维经过硼化物溶液浸渍，然后在1900℃～2500℃温度范围内进行高温热处理。采用X-ray衍射技术测定了渗硼前后炭纤维晶格参数和取向指数的变化。研究了渗硼对炭纤维力学性能和微观结构的影响。结果表明渗硼显著地提高了炭纤维的模量，而强度并没有降低，同时增加了晶格尺寸，改善了纤维的结构取向。
The boron modification of PAN-based carbon fibers was studied.The HTA-3K carbon fibers were impregnated in borate solution and then heated in range of 1 900 ℃～2500 ℃. The crystallite size and the degree of preferred orientation were characterized by X-ray diffraction. The effect of boron on the mechanical properties and microstructure of carbon fiber was investigated. It was found that the tensile modulus of boron-doped CF obviously increased, while the tensile strength did not decrease. It is shown that interplanar spacing (d002) decreased and crystallite size (La, Lc) and the degree of preferred orientation increased after doping boron.
参考文献
| [1] | Agrawal A;Yinnon H;Uhlmann D R .Boron modification of carbon fibers[J].Journal of Materials Science,1986,21:3455-3466. |
| [2] | Jones L E;Thrower P A .Influence of boron on carbon fiber microstructure,physical properties,and oxidation behavior[J].CARBON,1991,29(02):251-265. |
| [3] | Debolt H E;Andover Mass .Carbon filament coating with boron and method of making same[P].US 4,142,008,1979. |
| [4] | 宇野博文;今井义隆 .超高弹性黑铅纤维制备方法[P].特开平JP 2-200819,1990. |
| [5] | 田艳红,常维璞,沈曾民,田明.炭纤维硼改性对其力学性能的影响[J].新型炭材料,1999(01):69-72. |
| [6] | Rose P G.Grystal growth in PAN-based carbon fibers[M].London,1974:18-22. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%