以羧甲基纤维素(CMC)为粘结剂、比表面积为2 325 m2/g的粉状活性炭为原料,考察了成型活性炭的制备及其对甲烷吸附性能的影响.正交实验结果表明,影响甲烷体积吸附量的因素由大到小依次为:成型压力＞热处理温度＞热处理时间＞粘结剂的添加比例,并且得出了这种成型活性炭的最佳成型工艺,即:成型压力62.5 Mpa,热处理温度250 ℃,热处理时间90 min,粘结剂质量添加比例20 %.用最佳条件制备的成型活性炭在298 K和3.6 Mpa下对甲烷的体积吸附量可达167.9.
参考文献
| [1] | Lozano-Castello D.;Cazorla-Amoros D.;Linares-Solana A.;Quinn DF. .Activated carbon monoliths for methane storage: influence of binder[J].Carbon: An International Journal Sponsored by the American Carbon Society,2002(15):2817-2825. |
| [2] | S.Biloe;V.Goetz;S.Mauran .Characterization of adsorbent composite blocks for methane storage[J].Carbon: An International Journal Sponsored by the American Carbon Society,2001(11):1653-1662. |
| [3] | Wenming Qiao;Yozo Korai;Isao Mochida et al.Preparation of activated carbon form Ⅱ. Roles of activated carbons on the strength of activated carbon from using a thermoplastic polymer as binder[J].New Carbon Materials,2001,16(02):1-7+13. |
| [4] | 温斌;张鹏;王琪 .甲烷在活性炭上吸脱附行为的研究[J].天然气化工,1998,23:8-12. |
| [5] | D. Lozano-Castello;J. Alcaniz-Monge;M.A. de la Casa-Lillo .Advances in the study of methane storage in porous carbonaceous materials[J].Fuel,2002(14):1777-1803. |
| [6] | 宋燕,凌立成,李开喜,刘朗,樊彦贞.粘结剂添加量及后处理条件对成型活性炭甲烷吸附性能的影响[J].新型炭材料,2000(02):6-10. |
| [7] | 杨常玲,宋燕,李开喜.成型工艺条件对活性炭甲烷吸附性能的影响[J].煤炭转化,2001(01):86-88. |
| [8] | 詹亮,李开喜,吕春祥,朱星明,宋燕,凌立成.超级活性炭的制备及其储氢性能初步研究[J].新型炭材料,2001(04):31-35. |
| [9] | 宋燕 .高比表面积活性炭的制备及其对天然气吸附储存性能研究[D].中国科学院山西煤炭化学研究所,2001. |
| [10] | 刘海燕,凌立成,刘植昌,乔文明,樊彦贞,刘朗.甲烷在高比表面活性炭上脱附行为的研究[J].天然气化工,1999(03):12-15. |
| [11] | 刘海燕,凌立成,刘植昌,乔文明,刘朗.甲烷在高比表面积活性炭上行为的初步研究[J].天然气化工,1999(01):6-9. |
| [12] | Chen XS.;Mays TJ.;Alcanizmonge J.;Cazorlaamoros D. Linaressolano A.;Mcenaney B. .THEORETICAL AND EXPERIMENTAL STUDIES OF METHANE ADSORPTION ON MICROPOROUS CARBONS[J].Carbon: An International Journal Sponsored by the American Carbon Society,1997(9):1251-1258. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%