采用传统的熔融纺丝技术大量制备了定向性良好的纳米碳管/聚丙烯复合纤维.扫描电镜观察证实了纳米碳管在纤维里的定向性以及分散性都得到了较大的改善.通过拉伸实验测试了纳米碳管/聚丙烯复合纤维的力学性能,采用Weibull统计分析发现纳米碳管的添加显著提高了复合纤维的拉伸强度,当添加纳米碳管的质量分数达到3 %时,纤维强度最高,达到61MPa,超过聚丙烯纤维强度120%.复合纤维拉伸断口的形貌特征也证实了纳米碳管添加对复合纤维拉伸性能影响存在临界现象.
Well-aligned, long fibers composed of multi-walled carbon nanotubes (MWNTs) and polypropylene (PP) were fabricated by a conventional melt spinning technique. Scanning electron microscope (SEM) observations of the morphology revealed that both the alignment and dispersion of MWNTs in the matrix were improved. Mechanical properties of the composite fibers were studied by tensile testing and Weibull distribution, and it was found that their tensile strength was increased with addition of the carbon nanotubes. The maximum tensile strength of 61 Mpa was achieved at 3 w/% MWNT addition, 120 % more than that of the pure PP fibers. Moreover, a unique tensile rupture characteristic was found by SEM observations, which explained the critical phenomenon that the MWNT addition affects the tensile property of the MWNT composite fibers.
参考文献
| [1] | Vigolo B;Pénicaud A;Coulon C et al.Macroscopic fibers and ribbons of oriented carbon nanotubes[J].Science,2000,290:1331-1334. |
| [2] | Frank Ko;Yury Gogotsi;Ashraf Ali et al.Electrospinning of continous carbon nanotube-filled nanofiber yarns[J].Current Advances in Materials and Processes,2003,13:1161-1164. |
| [3] | Ya-Li Li;Kinloch I A;Windle A H .Direct spinning of carbon nanotube fibers from chemical vapor deposition[J].Science,2004,304:276-278. |
| [4] | Ericson LM;Fan H;Peng HQ;Davis VA;Zhou W;Sulpizio J;Wang YH .Macroscopic, neat, single-walled carbon nanotube fibers[J].Science,2004(5689):1447-1450. |
| [5] | Shofner M L;Rodríguez-Macías F J;Vaidyanathan R et al.Single wall nanotube and vapor grown carbon fiber reinforced polymers processed by EFF[J].Composites Part A:Applied Science and Manufacturing,2003,34:1207-1217. |
| [6] | Fan YY.;Cheng HM.;Su G.;Yu YD.;Shen ZH.;Li F. .Preparation, morphology, and microstructure of diameter-controllable vapor-grown carbon nanofibers[J].Journal of Materials Research,1998(8):2342-2346. |
| [7] | L. Valentini;J. Biagiotti;J. M. Kenny .Morphological characterization of single-walled carbon nanotubes-PP composites[J].Composites science and technology,2003(8):1149-1153. |
| [8] | Weibull W .A statistical theory of the strength of materials[J].Ing Vetensk Akad Proc,1939,151:1-45. |
| [9] | 童昕,赫秀娟,成会明.添加纳米碳管对高密度聚乙烯力学行为和结晶过程的影响[J].新型炭材料,2004(04):261-267. |
| [10] | 李莉香,李峰,英哲,杨全红,成会明.纳米碳管/聚合物功能复合材料[J].新型炭材料,2003(01):69-74. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%