以中间相沥青为前驱体制备高性能泡沫炭,在考察中间相沥青、Fe(NO3)3及其混合物热分解行为的基础上,着重研究了Fe(NO3)3对制备中间相沥青基泡沫炭的影响,揭示了Fe(NO3)3对泡沫炭孔泡结构的影响规律及其作用机制,初步研究了在泡沫炭炭化过程中形成的Fe/C之物相结构及其石墨化行为.结果表明,在不同的炭化温度下,Fe在泡沫炭中的存在形态各异;Fe物种的存在有利于提高泡沫炭的石墨化程度.
参考文献
| [1] | 成会明,刘敏,苏革,侯鹏翔,沈祖洪.泡沫炭概述[J].炭素技术,2000(03):30-32. |
| [2] | 李凯,栾志强.中间相沥青基炭泡沫[J].新型炭材料,2004(01):77-78. |
| [3] | 曹敏,张书,王永刚.制备条件对炭泡沫结构的影响[J].新型炭材料,2005(02):134-138. |
| [4] | Klett J.;Romine E.;Walls C.;Burchell T.;Hardy R. .High-thermal-conductivity, mesophase-pitch-derived carbon foams: effect of precursor on structure and properties[J].Carbon: An International Journal Sponsored by the American Carbon Society,2000(7):953-973. |
| [5] | Kearns K.Graphitic carbon foam processing[A].Florida,1997:835-847. |
| [6] | Klett J W .Process for making carbon[P].US 6033506,2000. |
| [7] | James W.Klett;April D.McMillan;Nidia C.Gallego;Timothy D.Burchell;Claudia A.Walls .Effects of heat treatment conditions on the thermal properties of mesophase pitch-derived graphitic foams[J].Carbon: An International Journal Sponsored by the American Carbon Society,2004(8/9):1849-1852. |
| [8] | Nidia C. Gallego;James W. Klett .Carbon foams for thermal management[J].Carbon: An International Journal Sponsored by the American Carbon Society,2003(7):1461-1466. |
| [9] | 金鸣林,冯安祖,史美仁,陈新桂,张初永,李应海,朱静,张晓燕.煤沥青与橡胶改质筑路油族组成分析[J].南京化工大学学报,1999(04):14-17. |
| [10] | 何选明;李其祥;赵敏伦.煤沥青中添加Fe(NO3)3的改质效果及其机理初探[J].炭素技术,1995(01):8-12. |
| [11] | 林起浪,李铁虎,单玲,陈彦.炭材料用基体前驱体沥青的改性研究[J].新型炭材料,2001(02):27-31. |
| [12] | 吴卫泽,朱珍平,刘振宇.Fe/C复合纳米材料的制备研究[J].新型炭材料,2002(01):4-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%