以乙炔(C2H2)为碳源,铁为催化剂,通过化学气相沉积技术在单晶硅衬底上制备了碳纳米带.采用场发射SEM、TEM、激光Raman光谱等先进分析手段对其形态和结构进行了表征.研究发现:碳纳米带是一种准二维材料,厚度约30nm,宽度在几百纳米,长度在100μm量级.碳纳米带的碳层沿着与其生长轴方向一致的(002)晶向排列,碳层的边缘都弯曲折叠成封闭结构.碳纳米带中碳层的排列不很平直,其中存在大量的层错.由此认为碳纳米带可用于能源等领域.
参考文献
| [1] | Kroto H W;Heath J R;Brien S C O et al.C-60-buckminster fullerene[J].Nature,1985,318:162-163. |
| [2] | Iijima S .Helical microtubules of graphitic carbon[J].Nature,1991,354:56-58. |
| [3] | Ugarte D .Curling and closure of graphitic networks under electron-beam irradiation[J].Nature,1992,359:707-709. |
| [4] | Zhang GY.;Jiang X.;Wang EG. .Tubular graphite cones[J].Science,2003(5618):472-474. |
| [5] | 陈秀琴.CVD法制备微旋管状炭纤维的微观形貌[J].新型炭材料,2000(03):23-27. |
| [6] | 章海霞,王晓敏,王海英,刘旭光,许并社.电弧法制备洋葱状富勒烯的工艺研究[J].新型炭材料,2004(01):61-64. |
| [7] | 戈敏,沈曾民.气相催化裂解法制备微米级螺旋形炭纤维的研究[J].新型炭材料,2003(01):31-36. |
| [8] | 王茂章,李峰,杨全红,成会明.由不同碳源合成及制备纳米碳管的进展[J].新型炭材料,2003(04):250-264. |
| [9] | 雷中兴,刘静,王建波,李轩科,汪厚植.催化剂结构与形态对碳纳米管生长的影响[J].新型炭材料,2003(04):271-276. |
| [10] | 刘云芳,沈曾民,马宝海,于建民.碳源对碳纳米管形态的影响[J].新型炭材料,2003(04):295-299. |
| [11] | 卢怡,朱珍平,刘振宇.催化剂对爆炸法合成碳纳米管的影响[J].新型炭材料,2004(01):1-6. |
| [12] | 李天保,许并社,韩培德,张艳,王晓敏,刘旭光,市野濑英喜.洋葱状富勒烯的CCVD法制备及其形貌特征[J].新型炭材料,2005(01):23-27. |
| [13] | Boenm H P .Carbon form carbon monoxide disproportionation on nickel and iron catalysts:morphological studies and possible growth mechanisms[J].CARBON,1973,11:583-590. |
| [14] | Murayama H;Maeda T .A novel form of filamentous graphite[J].Nature,1990,345(28):791-793. |
| [15] | Soneda Y;Makino M .Formation and texture of carbon nanofilaments by the catalytic decomposition of CO on stainless-stell plate[J].Carbon,2000,38:475-494. |
| [16] | 杨子芹,沈曾民,陈晓红,查旭峰.Co催化热分解制备弯曲状碳纳米管的研究[J].新型炭材料,2000(02):34-38. |
| [17] | Tsu R;Gonzalez J H;Hernandez I C .Observation of splitting of the mode and two phono spectrum in graphite[J].Solid State Communications,1978,27:507-511. |
| [18] | 唐致远,庄新国,李建钢,薛建军.炭材料贮锂机理研究的现状[J].新型炭材料,2001(04):71-76. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%