研究了微孔SiO2膜的气体渗透性能.气体渗透数据表明,由于微孔SiO2膜存在着一定的孔径分布,其渗透机理比较复杂.当膜的孔径大于并接近分子的动力学直径时,其渗透由择形扩散控制;而当膜的孔径大于而不接近分子的动力学直径时,对于非凝聚的小分子气体其渗透受努森扩散控制;对于可凝性气体其渗透将受多层扩散和毛细管凝聚的控制.单组份正/异丁烷气体在25℃、压差为0.06 MPa时的理想分离系数为1.8;1:1的正/异丁烷混合气的分离系数为8.4.
参考文献
| [1] | Bhave R R.Inorganic membranes synthesis,characteristics and applications[M].New York: Van Nostrand Reinhold,1991 |
| [2] | Brinker C J;Ward T L;Sehgal R et al."Ultramicroporous"silica-based supported inorganic membrane[J].Journal of Membrane Science,1993,77:165-179. |
| [3] | Uhlhorn R J R;Keizer K;Burggraaf A J .Gas transport and separation with ceramic membranes.Part Ⅱ.Synthesis and separation properties of microporous membranes[J].Journal of Membrane Science,1992,66:271-281. |
| [4] | Yan Y H;Davis M E;Gavalas G R .Prepation of zeolite ZSM-5 membranes by in-suit crystallization on porourous α-Al2O3[J].Industrial and Engineering Chemistry Research,1995,34:1652-1661. |
| [5] | 鲍筠,谷景华.用聚合溶胶-凝胶法制备纳米孔陶瓷膜[C].材料科学与工程(1997增刊)(全国第二届溶胶-凝胶科学技术学术会议论文集),1997:253～256. |
| [6] | 谷景华 .应用溶胶—凝胶法制催化无机膜的研究[D].中国科学院大连化学物理研究所,1994. |
| [7] | Vroon Z A E P.Synthesis and transport studies of thin ceramic support zeolite(MFI)membranes[J].Netherlands:University of Twente,1995 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%