以聚乙烯醇(PVA)和硼酸(H3 BO3)的凝胶体为纺丝载体,由聚四氟乙烯(PTFE)分散乳液通过凝胶纺丝法制备PTFE/PVA初生中空纤维,经烧结去除载体,得到聚四氟乙烯中空纤维膜.通过在成膜体系中引入纳米无机粒子碳酸钙(CaCO3),经后拉伸得到具有界面微孔结构的PTFE/CaCO3杂化中空纤维膜.研究了PVA和H3 BO3的络合机理,并讨论了CaCO3对杂化中空纤维膜性能及结构的影响.通过对膜的表面形貌观察表明所得PTFE中空纤维膜是一种均质膜,形成的界面微孔结构不同于PTFE双向拉伸产生的纤维-结点状裂隙孔结构,界面微孔的数量和孔径随着后拉伸倍数的增加呈增大的趋势.
参考文献
| [1] | WinstonHo W S;Sirkar K K;张志城.Membrane Handbook[M].北京:海洋出版社,1999:424-526. |
| [2] | Goessi M;Tervoort T;Smith P .Melt-spun poly(tetrafluoroethylene) fibers[J].Journal of Materials Science,2007(19):7983-7990. |
| [3] | Bacino J;Gore W L;Associates Inc .USA.Thin porous PTFE film and a mamfacturing method[P].US Pat:5476589,1995-12-19. |
| [4] | Gryta M .Influence of polypropylene membrane surface porosity on the performance of membrane distillation process[J].Journal of Membrane Science,2007(2):67-78. |
| [5] | Liu YL;Yu CH;Lai JY .Poly(tetrafluoroethylene)/polyamide thin-film composite membranes via interfacial polymerization for pervaporation dehydration on an isopropanol aqueous solution[J].Journal of Membrane Science,2008(1/2):106-115. |
| [6] | 陈珊妹,李敖琪.双向拉伸PTFE微孔膜的制备及其孔性能[J].膜科学与技术,2003(02):19-22. |
| [7] | 胡晓宇,肖长发,安树林,王照旭.PU/PVDF共混中空纤维膜结构与性能[J].膜科学与技术,2007(06):97-100. |
| [8] | Feng CS;Wang R;Shi BL;Li GM;Wu YL .Factors affecting pore structure and performance of poly(vinylidene fluoride-co-hexafluoro propylene) asymmetric porous membrane[J].Journal of Membrane Science,2006(1/2):55-64. |
| [9] | 马训明,郭玉海,陈建勇,孙芳.聚四氟乙烯纤维的凝胶纺丝[J].纺织学报,2009(03):10-12,17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%