使用高分辨电子显微镜(TRTEM)观察分析了中碳和中高碳贝氏体钢贝氏体铁素体-奥氏体取向关系及贝氏体铁素体条束内残留奥氏体.贝氏体钢中上贝氏体-奥氏体界面同时存在K-S关系和N-W关系或单独存在K-S关系.标定结果证明,[100]α1∥[110]γ∥[111]α2,(011)α1//(111)γ∥(110)α2,以及[111]α∥[110]γ,(110)α//(111)γ.透射电镜观察发现,贝氏体铁素体内有形貌及尺度不同的残留奥氏体膜存在,它们把贝氏体铁素体分割或包围成不同层次的结构单元,以残留奥氏体膜为分界面确定了贝氏体铁素体不同层次的精细结构单元及其尺度.贝氏体铁素体条束由亚片条、亚单元和基本单元(或称为超亚单元)组成.多数亚片条,亚单元和基本单元尺度分别在25～80nm、25～80nm和50～30nm不等.
参考文献
| [1] | Smith G V;Mehl R F.Lattice relationships in decomposition of austenite to pearlite,bainite and martensite[J].Transactions of The American Institute of Mining and Metallurgical Engineers,1942(1950):211-226. |
| [2] | Hoekstra S.An accurate and general method of determning habit planes and orietation relationship in bainitic steels and a verification of the IPS theory[J].TMS-AIME,1982:1017-1021. |
| [3] | Sandvik B P J;Wayman C M .Characteristics of lath maaensite: Part 1. Crystallographic and substructural features[J].Metallurgical and Materials Transactions,1983,14(05):809-822. |
| [4] | 方鸿生;王家军;杨志刚;李春明，薄祥正，郑燕康.贝氏体相变[M].北京:科学出版社,1999:115,229-254. |
| [5] | 李凤照;顾英妮;敖青 .贝氏体巨型台阶和界面结构[J].金属热处理学报,1998,19(03):13-16. |
| [6] | Reynolds W T;LI F Z;Shui C K;Aaronson H I .The incomplete transformation phenomenon in Fe-C-Mo alloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1990,21(06):1433-1463. |
| [7] | 俞德刚;朱钰如;陈大军 .Fe-C合金贝氏体铁素体的相变基元与类马氏体形貌贝氏体的形成[J].金属学报,1994,30(09):385-393. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%