采用纳米显微力学探针(Nano 不Identer Ⅱ)及透射电子显微镜,对使用不同时间的低合金耐热钢(12Cr1MoV)电厂主蒸汽管道的组织及性能进行分析研究.结果表明:随着运行时间的延长,细小碳化物颗粒不断在铁素体基体中析出,使基体强化,管样显微硬度提高;但在晶界出现聚集长大的碳化物.若运行时间过长,最终可能因晶界碳化物的粗大而产生沿晶断裂.本文分析的已使用30×104h的主蒸汽管道仍能继续运行使用.
参考文献
| [1] | Brian J Cane;TWI;Granta Park.Risk and life management of ageing power plant assets[J].ICOLM,2000:1-33. |
| [2] | Viswnathan R.Damage mechanisms and life assessment of high-temperature components[M].ASM International,1989:189. |
| [3] | Li Yaojun et al.Study on behavior of material aging and remanant life of steel 12CrlMoV used in super-heater[R].Report of TPRI,1995. |
| [4] | Li Yaojun .The method of quantitative metallographic analysis[R].Report of TPRI,1999. |
| [5] | 王艳丽 .纳米压入法表征材料微区力学性能的研究[D].北京科技大学,2001. |
| [6] | W C Oliver;G M Pharr .An improved technique for deter mining hardness and elastic modulus using load and displacement sensing indentat ion experiments[J].Journal of Materials Research,1992,7(06):1564-1583. |
| [7] | 林志,王艳丽,林均品,陈国良.纳米力学探针的基本原理及其应用实例[J].航空材料学报,2001(04):56-62. |
| [8] | 宋维锡.金属学[M].北京:冶金工业出版社,1980 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%