采用氩气保护烧结制备了多孔TiNi合金,并用图像分析的方法对其孔隙和孔隙率进行了研究.结果表明:粉末粒度和压制压力影响压坯中的孔隙和粉末颗粒之间的结合,从而影响烧结产物的孔隙;烧结温度和烧结时间是影响多孔TiNi合金孔隙的重要因素;980℃烧结时孔隙形成发展过程分为三个阶段:新孔形成、孔隙的聚集和孔隙的收缩,烧结8h所得到的多孔TiNi合金的孔隙率较高;1000℃下烧结0.5h孔隙已经基本形成,延长时间孔隙率变化不大.
参考文献
| [1] | Lipscomb I P;Nokes L D M.The application of shape memory alloy in medicine[M].Suffolk,UK:Mechanical Engineering Publications,1996 |
| [2] | Ryhanen J;Kallioinen M;Tuukkanen J;Lehenkari P;Junila J;Niemela E;Sandvik P;Serlo W .Bone modeling and cell-material interface responses induced by nickel-titanium shape memory alloy after periosteal implantation.[J].Biomaterials,1999(14):1309-1317. |
| [3] | 诸幼义 .形状记忆合金在医学应用研究的新动向[J].医用生物力学,1995,10(02):1-3. |
| [4] | 孙世清,郭志猛,殷声.TiNi形状记忆合金及其多孔体[J].材料导报,2001(02):64-66. |
| [5] | B. Y. Li .Porous NiTi alloy prepared from elemental powder sintering[J].Journal of Materials Research,1998(10):2847-2851. |
| [6] | 费多而钦科;北京钢铁学院粉末冶金教研室.粉末冶金原理[M].北京:冶金工业出版社,1974 |
| [7] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1982 |
| [8] | Zhang Ning;Babayang Khosrovabadi P;Lindenhovius J H .TiNi shape memory alloys prepared by normal sintering[J].Materials Science and Engineering,1992,A150:263-270. |
| [9] | 松山芳治;三谷裕康;铃木寿;周安生,高一平,王颖.粉末冶金学[M].北京:科学出版社,1978 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%