采用压痕-急冷法测试了单相3Y-ZrO2及3Y-ZrO2/Fe3Al复合材料的抗热震性能,并与急冷-强度法的测试结果进行了对比分析.试验结果表明,两种方法之间存在一致性.两种复合材料比基体的抗热震性均有较大幅度的提高.压痕-急冷法与急冷-强度法相比免去了热震后的强度测试,不同温度下热震可以采用同一试样,而后者在不同热震温差下,必须使用新的试样.
参考文献
| [1] | 李嘉,尹衍升,谭训彦.ZrO2（3Y）/Fe3Al复合材料的显微结构及性能[J].无机材料学报,2004(01):189-195. |
| [2] | Andersson T.;Rowcliffe DJ. .INDENTATION THERMAL SHOCK TEST FOR CERAMICS[J].Journal of the American Ceramic Society,1996(6):1509-1514. |
| [3] | T.Yoshimoto;S.Ishihara;T.Goshima;A.J.McEvily;T.Ishizaki .An improved method for the determination of the maximum thermal stress induced during a quench test[J].Scripta materialia,1999(5):553-559. |
| [4] | M. Collin and D. Rowcliffe .ANALYSIS AND PREDICTION OF THERMAL SHOCK IN BRITTLE MATERIALS[J].Acta materialia,2000(8):1655-1665. |
| [5] | CemailAksel;Paul Warren .Thermal shock parameters [ R, R'" and R"" ] of magnesia-spinel composites[J].Journal of the European Ceramic Society,2003,23:301-308. |
| [6] | PetterssonP;Shen Z .Thermal shock resistance of α/β-sialon ceramic composites[J].Journal of the European Ceramic Society,2001,21:999-1005. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%