研究了形变热处理对2091型Al-Li合金显微组织和力学性能的影响,结果表明,固溶+8%变形+双级时效可以使合金获得良好的强塑性配合.合金中主要强化相δ'(Al3Li)适宜的粒度、析出相S'(Al2CuMg)分散沉淀、晶界上平衡相析出量的减少以及δ'无沉淀析出带(PFZ)的窄化,是合金强塑性改善的主要原因.
参考文献
| [1] | 尹登峰,郑子樵.铝锂合金研究开发的历史与现状[J].材料导报,2003(02):18-20. |
| [2] | 魏建锋 .铝锂合金研制进展[J].稀有金属材料与工程,1994,22(01):1-6. |
| [3] | Gable B M;Zhu A W;Csontos A A;Starke E A.The role of plastic deformation on the competitive microstructure evolution and mechanical properties of anovel Al-Li-Cu-X alloy[J].Journal of Light Metals,2001(01):1-14. |
| [4] | Singh A K;Saha G G;Gokhale A A et al.Evolution of texture and microstructure in a thermo-mechanically processed Al-Li-Mg alloy[J].Metallurgical and Materials Transactions,1998,294:665-675. |
| [5] | Zdeněk Drozd;Zuzanka Trojanová;Stanislav Kúdela .Deformation behaviour of Al-Li-Mg alloys[J].Journal of Alloys and Compounds,2004,378:192-195. |
| [6] | 肖纪美.合金相与相变[M].北京:冶金工业出版社,2004:212-216. |
| [7] | 黄楚云,石其年.快速冷凝Al-Li-Cu-Mg-Zr合金时效工艺研究[J].热加工工艺,2004(01):29-31. |
| [8] | 尤世武.Al-Li合金形变热处理的织构组织研究[J].理化检验-物理分册,2001(06):240-242,245. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%