采用半连续铸造制成了Cu-17Zn-0.4Cr合金(质量分数,%),通过硬度、强度测定和显微组织的观察,对不同热轧态Cu-17Zn-0.4Cr合金进行了研究.结果表明:Cu-Zn-Cr合金是典型的时效强化型合金;在本实验条件下,该合金较好的加工工艺为快速热轧淬火(开轧温度为930℃)+450℃时效1h;快速热轧淬火工艺具有保留加工强化的作用.
参考文献
| [1] | 罗丰华 .高速列车异步牵引电动机转子专用铜合金的研究[D].中南工业大学,1999. |
| [2] | 邓至谦;周善初.金属材料热处理[M].长沙:中南工业大学出版社,1989:71. |
| [3] | 曹玲飞,汪明朴,李周,王艳辉,尹志民.Cu-17.0Zn-xCr合金形变热处理[J].中国有色金属学报,2002(01):145-150. |
| [4] | 张生龙 .Cu-Cr-Zr和Cu-Zn-Cr-Zr合金时效特性研究[D].中南大学,2002. |
| [5] | Morris M A;Leboeuf M .Recrystallization mechanisms in a Cu-Cr-Zr alloy with a bimodal distribution of particles[J].Materials Science and Engineering,1994,188:255-265. |
| [6] | Dahmen U;Wtcomb M J;Westmacott K H et al.Morphology of Cr precipitates in an overaged Cu-0.3 % Cr alloy[J].Scripta Metallurgica et Materialia,1988,22:1867. |
| [7] | Knight R W;Wilke P.Precipitation of chromium in copper and copper-nickel base alloys[J].Metallurgical and Materials Transactions,1973(04):2389. |
| [8] | Luo C P;Dahmen V;Westmacott K H et al.Morphology and crystallography of Cr precipitates in a Cu-0.33wt % Cr alloy[J].Acta Materialia,1994,6(42):923. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%