研究镁合金基体上进行预处理及电镀Sn、Zn处理后,在190℃进行扩散热处理后的镀层结构.通过XRD、SEM及Darken-Garry理论分析不同热扩散时间后,不同镀层、镀层与镁合金基体之间的微观形貌和相结构的变化.研究表明,镁合金表面镀锌和镀锡后,在190℃处理过程中,锡逐渐扩散至镀锌层内部,并与镁形成了Mg2Sn化合物,锌和镁间并未形成化合物及固溶体.单独镀锡层锡与镁的扩散速度大于Zn/Sn叠层中锡与镁的扩散速度.在保温过程中单镀锌层并未与镁合金发生明显的扩散反应,只是镀锌层结构发生了改变.
参考文献
| [1] | Isao Nakatsugawa;Hidenori Takayasu;Katsuyuki Araki .Electrochemical Corrosion Studies of Thixomolded AZ91D Alloy in Sodium Chloride Solution[J].Materials Science Forum,2003(Pt.2):845-850. |
| [2] | H. Tsubakino;A. Yamamoto;K. Sugahara .Corrosion Resistance in Magnesium Alloys and Deposition Coated Magnesium Alloy[J].Materials Science Forum,2003(Pt.2):915-920. |
| [3] | Ambat R;Aung R;Zhou W .Evaluation of microstructure effect son corrosion behavior of AZ91D magnesium alloy[J].Journal of Corrosion Science,2000,42:1433-1455. |
| [4] | 张英杰,杨显万,屠振密,杨哲龙,张景双.代镉锡锌合金的电镀工艺与机理[J].中国有色金属学报,1997(04):57-60. |
| [5] | Ryoich Yoshihave;Himeji .Surface treated steel sheet with less environmental impact for electronic components,excellent in solder wettability,a rust-proof property and a whisker-proof property[P].US 6818322,2004. |
| [6] | 程沪生.热扩散法镀黄铜丝[J].材料保护,2004(09):53-54. |
| [7] | Shigematsu I.;Saitou N.;Shimojima K.;Nakamura M. .Surface treatment of AZ91D magnesium alloy by aluminum diffusion coating[J].Journal of Materials Science Letters,2000(6):473-475. |
| [8] | Zhang M X;Kelly P M .Surface alloying of AZ91D alloy by diffusion on coating[J].Journal of Materials Research,2002,17:2447-2479. |
| [9] | 朱立群,刘慧丛,李卫平,宋光龄.AZ91D镁合金表面热扩散渗锌膜层研究[J].北京航空航天大学学报,2005(01):8-12. |
| [10] | 张允诚;胡如南;向荣.电镀手册[M].北京:国防工业出版社,1998:412-417. |
| [11] | 余永宁.金属学原理[M].北京:冶金工业出版社,2000:208-214. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%