为提高多元替代低钴贮氢合金MlNi3.8 Al027 Mn0.36 Co0.24 Cu0.15 Cr0.1 Zn0.05 Fe0.05的电化学性能,研究了850℃与1050℃两种温度退火对合金的微观结构、组织以及电化学性能的影响.XRD分析表明,退火降低了合金的晶格应力和缺陷,同时使得合金的单胞体积增大.电化学测试结果表明,退火合金的放电容量明显提高,其中1050℃退火后合金的最大放电容量达到315mAh/g,比铸态合金提高26mAh/g.退火使得合金的高倍率放电性能略有降低,但仍达到96%,退火提高了合金的循环稳定性.
参考文献
| [1] | 李全安,桑革,李建文,陈云贵,唐定骧,涂铭旌.多元低钴稀土基贮氢合金及其电极特性[J].稀土,2000(04):30-33,46. |
| [2] | Ping Li;Xin-Lin Wang;Yang-Huan Zhang .Research of low-Co AB_5 type rare-earth-based hydrogen storage alloy electrodes[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2003(1/2):310-314. |
| [3] | 魏范松 .低Co贮氢合金ReNi3.5Co0.3Mn0.3Al0.4Fe0.5-326[Z]. |
| [4] | H.C. Lin;K.M. Lin;H.T. Chou .Effects of annealing and NaOH pretreatment on an LmNi_(3.65)Al_(0.34)Mn_(0.27)Co_(0.74) hydrogen storage alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2003(1/2):281-287. |
| [5] | 马志鸿;陈立新;顾巍 等.热处理对低Co贮氢合金Ml(NiCoMnAlFe)5电化学性能的影响[J].中国有色金属学报,2001,10(01):220-222. |
| [6] | 朱光明,雷永泉,陈立新,王启东.Ti对Ml（NiCoMnTi）5合金相结构和充放电循环性能的影响[J].金属学报,2001(09):935-942. |
| [7] | 张书凯,雷永泉,吕光烈,陈立新,舒康颖,李世群,王启东.过化学计量比无钴合金Ml（Ni0.82Mn0.07Al0.06Fe0.05）5.4的晶体结构和电化学性能[J].稀有金属材料与工程,2002(01):44-47. |
| [8] | 马志鸿,雷永泉,陈立新,顾巍.热处理对Ml（NiCoMnAl）4.76合金的电化学性能的影响[J].稀有金属材料与工程,2000(04):255-257. |
| [9] | 吴朝玲,陈云贵,李锋,陶明大,涂铭旌,唐定骧.Effects of Strip Casting and Annealing on Electrochemical Properties of LPCNi3.55Co0.75Mn0.4Al0.3 Hydrogen Storage Alloys[J].稀土学报(英文版),2004(02):254-258. |
| [10] | 朱光明 .稀土成分对RE(NiCoMnTi)<,5>贮氢合金电化学性能影响的研究[D].浙江大学,1997. |
| [11] | 刘永锋,金勤伟,高明霞,朱云峰,张志鸿,潘洪革.热处理对La0.7Mg0.3Ni2.8Co0.5贮氢合金电化学性能的影响[J].稀有金属材料与工程,2003(11):942-945. |
| [12] | GUO Jinghong,CHEN Demin,Liu Guozhong,YANG Ke,MA Jun.Research of heat treatment of low-Co AB5 type hydrogen storage alloys for MH-Ni batteries[J].稀有金属(英文版),2003(03):175-178. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%