将Cr以铬铁的形式加入到FeNiMoCu系预合金粉末中,经充分混合后单轴600MPa下压制,然后分别采用冷压烧结、烧结热锻和复烧工艺,研究铬对FeNiMoCu系预合金粉末烧结密度、组织及性能的影响.实验结果表明,添加到预合金粉末中的铬在1573K温度烧结时可均匀扩散到组织中,使组织性能得到改善;随添加的铬量和复烧温度的提高,微观组织硬度和表观硬度逐渐增加,经热锻及热锻复烧可获得较高的烧结密度和硬度.当复烧温度为1573K时,Fe-1.5Cr-2.0Ni-0.85Mo-1.7Cu-0.5C获得的密度为7.71 g/cm3,硬度为105HRB;Fe-4.0Cr-3.0Ni-0.85Mo-1.7Cu-0.5C获得的密度为7.63g/cm3,硬度为105HRB.
参考文献
| [1] | Randall M. German .Manipulation of Strength During Sintering as a Basis for Obtaining Rapid Densification without Distortion[J].Materials transactions,2001(7):1400-1410. |
| [2] | 古里维契;高后秀.粉末钢的热处理[M].天津:天津大学出版社,1990:23-56. |
| [3] | 李绍忠 .我国汽车用粉末冶金结构零件的现状与发展[J].粉末冶金技术,1996,24(02):139-144. |
| [4] | 毛志强.粉末冶金零件在汽车上的应用[J].粉末冶金工业,2003(01):8-11. |
| [5] | O. Lame;D. Bellet;M. Di Michiel .Bulk observation of metal powder sintering by X-ray synchrotron microtomography[J].Acta materialia,2004(4):977-984. |
| [6] | Campos M;Sanchez D;Torralba J M .Sintering behaviour improvement of a low Cr-Mo prealloyed powder stell through Mn additions and others liquid phase promoters,materials processing technology[J].Journal of Materials Processing Technology,2003,143:464-469. |
| [7] | Srinivasan N S;Dyanmic .Study of changes in structure and morphology during the heating and sintering of iron powder[J].Powder Technology,2002,124:40-44. |
| [8] | 郭庚辰.液相烧结粉末冶金材料[M].北京:化学工业出版社,2002:34-60. |
| [9] | 毛志强.粉末冶金零件在汽车上的应用[J].粉末冶金工业,2003(01):8-11. |
| [10] | Shimada;Kazuo .Developments of the production engineering in ferrous sintered machine parts[J].Journal of the Japan Society of Powder and Powder Metallurgy,1995,42(10):1093-1098. |
| [11] | Narasimhan KS. .Sintering of powder mixtures and the growth of ferrous powder metallurgy[J].Materials Chemistry and Physics,2001(1/3):56-65. |
| [12] | Youn-Che Kim;Shoji Goto .The effect of Cu addition method on dimensional change of Fe-Cu sintered compacts[J].Powder Metallurgy,2005,52:89. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%