采用异步轧制方法将成品工业取向硅钢板冷轧到0.10mm,然后在氢气热处理炉中进行三次再结晶高温退火,研究异步轧制硅钢极薄带退火过程中的再结晶过程.结果表明,硅钢极薄带在800℃退火时发生初次再结晶,晶粒取向主要为高斯取向,磁感低;900℃时初次再结晶中极少数晶粒突然长大而发生二次再结晶,对0.1mm的极薄带不能形成完善的高斯织构,磁性能下降;在1200℃时在合适的退火条件下可以发生三次再结晶,在极薄带中获得了取向集中的高斯织构和优异的磁性能.
参考文献
| [1] | Harase J;Shimizu R;Takahashi N .Effect of cold rolling reduction on the secondary recrystallization in 3%Si-Fe alloy[J].Journal of the Japan Institute of Metals,1990,54(04):381-387. |
| [2] | Arai K I;Ishiyama K .Rolled texture and magnetic properties of 3 % silicon steel[J].Journal of Applied Physics,1988,64:5352-5354. |
| [3] | Arai K;Ishiyama K .Tertiary recrystallization and magnetic properties of thin gage silicon steels[J].Bulletin Japan Inst Metals,1992,31(05):429-435. |
| [4] | 朱泉 .异步轧制实验研究[J].钢铁,1980,15(05):1-6. |
| [5] | Liang Z D;Xu J Z;Wang F.Determination of ODF of polycrystalline materials from incomplete pole figures[A].Tokyo,1981:1259-1265. |
| [6] | 梁志德;徐家桢;王福.织构材料的三维取向分析术-ODF[M].沈阳:东北工学院出版社,1986 |
| [7] | 高秀华;齐克敏 .异步轧制取向硅钢极薄带的冷轧织构研究[J].金属材料研究,2001,27(02):16. |
| [8] | 高秀华 .异步轧制取向硅钢极薄带的研究[D].东北大学,2002. |
| [9] | 毛卫民;赵新兵.金属的再结晶与晶粒长大[M].北京:冶金工业出版社,1994 |
| [10] | Nakashima S;Takashima K;Harase J .Effect of thickness on secondary recrystallization of Fe-3%Si[J].Acta Metallurgica Et Materialia,1994,42(02):539-547. |
| [11] | Harase J;Shimizu R;Takahashi N .Effect of cold rolling reduction on the secondary recrystallization in 3% Si-Fe alloy[J].Journal of the Japan Institute of Metals,1990,54(04):381-387. |
| [12] | 何忠治.电工钢[M].北京:冶金工业出版社,1996 |
| [13] | 高秀华,齐克敏,邱春林,叶何舟.热处理参数对异步轧制硅钢极薄带三次再结晶的影响[J].东北大学学报（自然科学版）,2005(01):55-58. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%