利用电阻-温度曲线测量,X射线衍射,金相观察等方法研究了Cu-24Al-3Mn合金β1母相非等温时效效应.结果表明,该合金具有很强的抗母相时效分解性能,以10℃/min速度加热至620℃时,合金仍具有良好的热弹性马氏体转变特性,可逆马氏体转变量高达92%以上.时效初期,马氏体相变点有所上升,但上升幅度仅10-15℃,后期变化不大.该合金母相状态时效时,析出相为γ2相.

参考文献

[1] Furlania A M;Stipcichb M;Romero R .Phase decomposition in a Cu-Zn-Al-Ti-B shape memory alloy[J].Materials Science and Engineering A,2005,392:386-393.
[2] Renhui Wang;Jianian Gui;Xiaomei Chen .EBSD and TEM study of self-accommodating martensites in Cu_(75.7)Al_(15.4)Mn_(8.9) shape memory alloy[J].Acta materialia,2002(7):1835-1847.
[3] Y. Sutou;R. Kainuma;K. Ishida .Effect of alloying elements on the shape memory properties of ductile Cu-Al-Mn alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(0):375-379.
[4] Garcir R J .Stabilization of martensite in CuZnAl shape memory alloys:effects of γ precipitatates and thermal cycling[J].Scripta Materialia,2000,42(06):531-536.
[5] N.Kayali;R.Zengin .Influence of aging on transformation characteristics in shape memory CuZnAl alloys[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2000(2):349-354.
[6] 王世伟,汪明朴.Cu基形状记忆合金的时效[J].中国有色金属学报,1994(03):65-68,105.
[7] Takezawa K;Sato S .Formation mechanism of α rod and αb plate in Cu-Zn and Cu-Zn-Al alloys[J].MATERIALS TRANSACTIONS,1991,32(08):766-773.
[8] Tadaki T;Okazaki H;Nakata Y et al.Atomic configuration studied by ALCHEMI and X-ray diffraction of a stabilized M18R martensite in a β phase Cu2Au2Zn alloy[J].Transactions of the Japan Institute of Materials,1990,31:941-947.
[9] 李周,汪明朴,郭明星.CuZnAl形状记忆合金母相时效过程中的组织变化[J].材料热处理学报,2004(03):10-13.
[10] 汪明朴,金展鹏,尹志民,徐根应.β1相非 等温时效对Cu-Al-Ni-Mn-Ti合金热弹性马氏体转变的影响[J].中国有色金属学报,1996(02):73-77.
[11] Kuwano N;Wayman C M .Some effect of parent phase aging on the martensite transformation in a CuAlNi shape memory alloy[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1984,15A:621-626.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%