采用金属粉末注射成形工艺制备出了0Cr17Mn11Mo3N高氮无镍奥氏体不锈钢(含氮0.78wt%),研究了固溶处理对力学性能和组织的影响.结果表明,固溶处理能极大改善材料组织和性能,未固溶处理试样组织主要为奥氏体、铁素体以及在晶界连成网状的Cr2N析出物,固溶处理后得到了均一的全奥氏体孪晶组织;固溶处理后力学性能大大提高,抗拉强度和伸长率分别为885MPa和26.0%,为未固溶试样的1.3倍和2.2倍;未固溶处理试样断口为沿晶和韧窝断裂特征,固溶处理试样为韧窝延性断裂特征.
参考文献
| [1] | Uggowitzer P J;Wolf-Friedrich B;Speidel M O .Metal injection molding of nickel-free stainless steels[J].Advances In Powder Metallurgy and Particulate Materials,1997,3(18):113-121. |
| [2] | Uggowitzer P J;Speidel M O;Wohlfromm H .P A N A C E A provides the answer to Ni allergy[J].Metal Powder Report,1998,53:49-52. |
| [3] | 颜慧成;刘浏.含氮奥氏体不锈钢及其冶金工艺[J].不锈开发,2003(04):1-19. |
| [4] | Simmous J W .Overview:High-nitrogen alloying of stainless steels[J].Materials Science and Engineering A-structural Materials Properties Microstructure and Processing,1996,207:15-169. |
| [5] | Rawers J C;Govier D;Doan R .Nitrogen addition to iron powder by mechanical alloying[J].Materials Science and Engineering A-structural Materials Properties Microstructure and Processing,1996,220:16-167. |
| [6] | Rhodes G O;Conway J J .High nitrogen stainless steels with high strength and corrosion resistance[J].Journal of Metals,1996,48(04):2-34. |
| [7] | Simmous J W .Overview:High-nitrogen alloying of stainless steels[J].Materials Science and Engineering A-structural Materials Properties Microstructure and Processing,1996,207:15-169. |
| [8] | 董瀚;Speidel M O.可持续发展的高氮奥氏体不锈钢[J].不锈钢,2004(02):1-7. |
| [9] | German R M.Powder injection molding[M].Princeton,MPIF,New Jersey,1990:207. |
| [10] | German R M;Bose A.Injection Molding of Metals and Ceramics[M].Princeton,MPIF,1997:1-2. |
| [11] | 李笃信,黄伯云.金属注射成形技术的研究现状[J].材料科学与工程,2002(01):136-139. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%