热压烧结化学镀法获得的Al2O3-Co+TiC-Co复合粉体制备超韧Al2O3-TiC-Co复合陶瓷.探讨了烧结温度、烧结气氛和分级保温时间对复合陶瓷微观形貌和力学性能的影响.结果表明,烧结温度为1550℃、真空保护并在750℃和1200℃各保温10 min制备的复合陶瓷力学性能最佳.采用最佳烧结工艺制备的Al2O3-TiC-8%Co复合陶瓷的平均抗弯强度和断裂韧性分别达到782MPa和8.0 MPa·m1/2.
参考文献
| [1] | Li H.;Sun JL.;Huang LP. .Effects of ductile cobalt on fracture behavior of Al2O3-TiC ceramic[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):17-20. |
| [2] | Luo YongMing;Li ShuQin;Chen Jian;Wang RuiGang;Li JianQiang;Pan Wei .Preparation and characterization of Al_2O3―Ti_3SiC_2 composites and its functionally graded materials[J].Materials Research Bulletin: An International Journal Reporting Research on Crystal Growth and Materials Preparation and Characterization,2003(1):69-78. |
| [3] | 郦剑;毛志远;葛曼珍 .精细陶瓷ATC及其对固体颗粒的抗力[J].中国学术期刊文摘,1996,2(07):12. |
| [4] | 邹正光,李金莲,陈寒元.高能球磨在复合材料制备中的应用[J].桂林工学院学报,2002(02):174-178. |
| [5] | 邵忠财,田彦文,翟玉春,李保山.ZrO2微粉表面化学镀镍动力学研究[J].无机材料学报,1999(03):397-402. |
| [6] | Chen L.;Kny E. .Reaction hot-pressed sub-micro Al_2O_3+TiC ceramic composite[J].International Journal of Refractory Metals & Hard Materials,2000(2/3):163-167. |
| [7] | 朱流,郦剑,凌国平,王幼文.超细ATC陶瓷制备及其干滑动磨损研究[J].浙江大学学报（工学版）,2005(12):1842-1846. |
| [8] | 果世驹.粉末烧结理论[M].北京:冶金工业出版社,1998:10-18. |
| [9] | GB 6569-1986.GB 6569-1986.工程陶瓷弯曲强度试验方法[S]. |
| [10] | GB 4161-1984.GB 4161-1984.金属材料平面应变断裂韧度KIC试验方法[S]. |
| [11] | 金志浩;高积强;乔冠军.工程陶瓷材料[M].西安:西安交通大学出版社,2000:33-56. |
| [12] | 李荣久.陶瓷-金属复合材料[M].北京:冶金工业出版社,1995:87. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%