采用机械合金化+热压工艺路线制备化学配比成分的单相Laves相Cr2Nb合金.研究了Cr、Nb元素粉经20h球磨后在1300℃不同时间热压所获得的Laves相Cr2Nb合金的组织性能.结果表明,采用机械合金化+热压工艺可以制备出高致密度的组织细小均匀的Laves相Cr2Nb合金,随着热压时间的延长,合金的致密度、晶粒尺寸和维氏硬度逐渐增大而断裂韧度逐渐减小.1300℃×30min的热压试样的平均晶粒尺寸达到亚微米级,致密度达到98.7%,断裂韧度达到5.07MPa·m1/2,与熔铸法制备的Laves相Cr2Nb相比,室温断裂韧性提高,实现了细晶组织对Laves相Cr2Nb合金的增韧效果.
参考文献
| [1] | Kwai S. Chan;David L. Davidson .The Fracture Resistance and Crack-Tip Micromechanics of In-Situ Intermetallic Composites[J].JOM,1996(9):62-67. |
| [2] | Takeyama M;Liu C T .Microstructure and mechanical properties of Laves-phase alloys based on Cr2Nb[J].Materials Science and Engineering,1991,A132:61-66. |
| [3] | Thoma DJ.;Nibur KA.;Chen KC.;Cooley JC.;Dauelsberg LB.;Hults WL. Kotula PG. .The effect of alloying on the properties of (Nb,Ti)Cr-2 C15 Laves phases[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(0):408-415. |
| [4] | 鲁世强,黄伯云,贺跃辉,邓意达,何双珍.Laves相合金的物理冶金特性[J].材料导报,2003(01):11-13,58. |
| [5] | Takasugi T.;Yoshida M.;Hanada S. .HIGH TEMPERATURE MECHANICAL PROPERTIES OF C15 LAVES PHASE CR2NB INTERMETALLICS[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(0):805-810. |
| [6] | Takasugi T;Yoshida M.TEM observation for deformation microstructures of two C15 NbCr2 intermetallic compounds[J].Intermetallics,2002(10):85-93. |
| [7] | K. S. Kumar;L. Pang;J. A. Horton .Structure and composition of Laves phases in binary Cr-Nb, Cr-Zr and ternary Cr-(Nb, Zr) alloys[J].Intermetallics,2003(7):677-685. |
| [8] | 鲁世强,黄伯云,贺跃辉.机械合金化对Laves相Cr2Nb因相热反应合成影响[J].航空学报,2003(06):568-572. |
| [9] | 鲁世强 .Laves相Cr<,2>Nb的机械合金化活化反应合成研究[D].中南大学,2003. |
| [10] | 鲁世强,肖璇,李鑫,董显娟,王克鲁,贺跃辉.低温退火温度对Laves相Cr2Nb固相热反应合成的影响[J].稀有金属材料与工程,2006(10):1535-1538. |
| [11] | 鲁世强,肖璇,李鑫,郑海忠,董显娟,王克鲁.低温退火时间对Laves相Cr2Nb固相热反应合成的影响[J].粉末冶金技术,2006(05):359-363. |
| [12] | Suryanayana C .Mechanical alloying[J].Progress in Materials Science,2001,46:1-184. |
| [13] | 尹衍升,李嘉,谭训彦,张金升.机械合金化-加压烧结制备Fe3Al金属间化合物[J].粉末冶金技术,2004(03):151-155. |
| [14] | C.T. Liu;J.H. Zhu .Physical metallurgy and mechanical properties of transition-metal Laves phase alloys[J].Intermetallics,2000(9/11):1119-1129. |
| [15] | 鲁世强,黄伯云,贺跃辉,何双珍,邓意达.Laves相合金的力学性能[J].材料工程,2003(05):43-47. |
| [16] | Sanboth L;Liaw P K;Liu C T et al.Cracking in Cr-Cr2 Nb eutectic alloys due to the themal stresses[J].Materials Science and Engineering,1999,A268:184-192. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%