研究了含1.5%Si-2.5%Mn-0.006%B和少量稀土、镍、铬、钛等合金的Si-Mn-B铸钢经900℃正火的显微组织和在销盘磨损和湿砂橡胶轮磨损条件下的抗磨损性能.钢中碳含量分别为0.17%、0.25%、0.34%、0.47%和0.53%.结果表明,碳含量较低时,主要形成粒状贝氏体,随着碳含量增加,钢的正火组织向针状贝氏体、上贝氏体和下贝氏体过渡,且组织变细.钢的硬度随碳含量增加而增大,冲击韧度随碳含量增加而下降.Si-Mn-B铸钢的耐磨性随碳含量的变化比较复杂.在销盘磨损条件下,使用低硬度玻璃砂磨料时,随着碳含量提高,磨损量减少,耐磨性增加,另外,材料的磨损量随着载荷的增加而增加,使用高硬度碳化硅磨料时,碳含量对磨损量的影响不明显.在湿砂橡胶轮磨损条件下,也呈现碳含量增加,磨损量减少的现象.
参考文献
| [1] | S.S. BABU;E.D. SPECHT;S.A. DAVID .In-Situ Observations of Lattice Parameter Fluctuations in Austenite and Transformation to Bainite[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2005(12):3281-3289. |
| [2] | 孙德勤,吴春京,谢建新.贝氏体钢的研究开发现状与发展前景探讨[J].机械工程材料,2003(06):4-7. |
| [3] | Wu H;LiuC;Zhao Z et al.Design of air-cooled bainitic microalloyed steel for a heavy truck front axle beam[J].Materials & Design,2006,27(08):651-656. |
| [4] | H. K. D. H. Bhadeshia .High Performance Bainitic Steels[J].Materials Science Forum,2005(0):63-74. |
| [5] | Hong-Sheng Fang;Qi Li;Bing-Zhe Bai .The Developing Prospect of Air-cooled Bainitic Steels[J].Materials Science Forum,2003(Pt.1):201-208. |
| [6] | Sakuma Y;Matsumura O;Takechi H .Mechanical properties and retained austenite in intercritically heat-treated bainite-transformed steel and their variation with Si and Mn additions[J].Metallurgical & Materials Transactions A:Physical Metallurgy & Materials Science,1991,22(02):489-498. |
| [7] | 张明星;康沫狂 .Si对低碳贝氏体钢组织和性能的影响[J].金属学报,1993,29(01):6-10. |
| [8] | F. G. Caballero;H. K. D. H Bhadeshia .Design of Novel High-Strength Bainitic Steels[J].Materials Science Forum,2003(Pt.2):1337-1342. |
| [9] | 桂洲,谭谆礼,白秉哲.Si对低碳贝氏体钢组织与性能的影响[J].金属热处理,2006(05):4-6. |
| [10] | G. Pintaude;D. K. Tanaka;A. Sinatora .The effects of abrasive particle size on the sliding friction coefficient of steel using a spiral pin-on-disk apparatus[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2003(1/6):55-59. |
| [11] | Izciler M.;Celik H. .Two- and three-body abrasive wear behaviour of different heat-treated boron alloyed high chromium cast iron grinding balls[J].Journal of Materials Processing Technology,2000(3):237-245. |
| [12] | 康沫狂.钢中贝氏体[M].北京:国防工业出版社,1990 |
| [13] | Chang L C .Microstructures and reaction kinetics of bainite transformation in Si-rich steels[J].Materials Science and Engineering A,2004,368(01):175-182. |
| [14] | Traint Sandra;Pichler Andreas;Hauzenberger Karl .Influence of silicon, aluminium, phosphorus and copper on the phase transformations of low alloyed TRIP-steels[J].Steel Research,2002(6/7):259-266. |
| [15] | Richardson R C D .Abrasion wear[J].Engineering,1969,208(5401):479-482. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%