研究了含1.55%Cu低碳钢在不同时效时间时的时效硬化行为.对经时效处理后的含铜高纯钢进行了显微硬度测试,应用金相显微镜(ZEISS)、X-射线衍射仪和JEM-2010型高分辨电子显微镜观察了含铜高纯钢等温时效过程的显微组织与结构,并分析了等温时效工艺与硬度、显微组织之间的对应关系.结果表明:时效温度越高,出现硬度峰值所需的时间越短,且峰值硬度也随之降低;550℃过时效阶段,铁素体晶粒中分布着大量的铜原子富集区,颗粒尺寸约20～72nm,随着等温时效时间的延长,富铜析出物不断粗化长大,从而导致硬度下降.
参考文献
| [1] | Montem arano T W .High Strength Low Alloy Steels in Nava Construction[J].Journal of Ship Production,1986,2(03):145-162. |
| [2] | Wang Shyi-Chin;Kao Powe .Effect of Alloying Elements on the Structure and Mechanical Properties of Ultra Low Carbon Bainitic Steels[J].J mater Sic,1993,28(19):5169-5175. |
| [3] | S.W. THOMPSON;G. KRAUSS .Copper Precipitation During Continuous Cooling and Isothermal Aging of A710-Type Steels[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1996(6):1573-1588. |
| [4] | Thompson S W .Continuous cooling transformation behavior in HSLA80 Steel[J].Metallurgical and Materials Transactions,1996,27A(06):1557-1571. |
| [5] | Deschamps M Militzer;W J Poole .Precipitation kinetics and strengthening of a Fe-0.8 wt% Cu alloy[J].ISIJ International,2001,41:196-205. |
| [6] | 王学敏,周桂峰,杨善武,贺信莱.含铜低合金高强钢的时效行为[J].钢铁研究学报,2000(05):40-45. |
| [7] | 朱丽慧,赵钦新,顾海澄,陆燕荪.关于钢中用铜合金化的再认识[J].钢铁,1999(03):71-75. |
| [8] | 王海燕,刘宗昌,任慧平.固溶温度对含铜钢时效行为的影响[J].包头钢铁学院学报,2004(01):41-44,51. |
| [9] | 刘宗昌,李文学,王海燕,安治国,任慧平.含铜高纯钢中有序结构的高分辨电子显微分析[J].包头钢铁学院学报,2005(02):137-143. |
| [10] | 刘宗昌.材料组织结构转变原理[M].北京:冶金工业出版社,2006:216-221. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%