运用H型双面电解槽,采用双面电解充氢法对海水中自然表面钛片进行恒电流电解充氢,研究了钛在海水中的阴极充氢过程.用X-射线衍射法对充氢后碎裂钛片进行检测,同时探讨了试样厚度、充氢电流密度和阳极氧化电位对于氢渗过程的影响.结果表明,表面膜是氢渗过程的控制因素;试样厚度增加,氢氧化峰值电流和峰值电流出现时间增加;峰值电流随充氢电流密度和B面氧化电位升高而增大,而峰值电流出现时间随充氢电流密度和B面氧化电位升高而减小.
参考文献
| [1] | 万晓景.金属的氢脆[J].材料保护,1979(02):11. |
| [2] | 朱祖芳.有色金属的耐腐蚀性及其应用[M].北京:化学工业出版社,1995:106. |
| [3] | 郭敏 .工业纯钛在海水中阴极极化条件下的氢脆研究[D].大连理工大学,2001. |
| [4] | Devanathan M A V;Stachurski Z .The Mechanism of Hydrogen Evolution on Iron in Acid Solutions by Determination of Permeation Rates[J].Journal of the Electrochemical Society,1964,111(05):619. |
| [5] | 王得明;黄显亚;朱祖芳.用超高压电镜研究钛中氢致破坏机理[J].稀有金属,1983(05):2. |
| [6] | Philips I I;Poole P;Shreir L L .Hydrogen Formation During Cathodic Polarization of Ti- Ⅱ.Effect of Temperature and pH of Solution on Hydride Growth[J].Corrosion Science,1974,14:533-542. |
| [7] | Pound B G .Hydrogen Ingress in Titanium[J].National Association of Corrosion Engineers,1991,47:99-104. |
| [8] | Covington L C .The Influence of Surface Condition and Environment on the Hydriding of Titanium[J].Corrosion,1979,35:378-382. |
| [9] | 袁晓姿.表面氧化层对低碳钢氢渗透行为的影响[J].腐蚀科学与防护技术,1995(02):151. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%