为了改善Ti基储氢合金的电化学性能,采用Cu元素部分替代Mn元素的方法,分析研究了Ti基储氢合金Ti0.3Zr0.225V0.25Mn0.20-xNi0.55Cux的相结构及电化学性能.结果表明,合金均由六方结构的C14型Laves主相和立方结构的TiNi第二相构成;随着Cu元素替代量的增大,合金的活化性能降低,而循环稳定性得到很大程度的改善.
参考文献
| [1] | Lee H H;Lee K Y;Lee J Y .[J].Journal of Alloys and Compounds,1996,239:63. |
| [2] | Lee SM.;Yu JS.;Lee PS.;Lee JY. .Application of flake metal as a surface modifier for the hydrogen absorbing intermetallic electrode of an Ni-MH rechargeable battery[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(0):339-345. |
| [3] | 朱云峰,潘洪革,刘永锋,李锐,金勤伟,王启东.新型钛钒系贮氢电极合金[J].中国有色金属学报,2003(03):680-684. |
| [4] | Gao X P;Sun Y M;Higuchi E et al.[J].Electrochimica Acta,2000,45:3099. |
| [5] | Chuang H J;Huang S S;Ma C Y et al.[J].Journal of Alloys and Compounds,1999,285:284. |
| [6] | XU Yan-hui,CHEN Chang-pin,LI Shou-quan,YING Tiao,WANG Qi-dong.High-temperature electrochemical performance and |
| [7] | 张勇,郭生武,罗东,柳永宁.Cr对TiMn基贮氢电极合金活化性能及电化学容量的影响[J].稀有金属材料与工程,2000(04):262-265. |
| [8] | 雷永泉.新能源材料[M].天津:天津大学出版社,2000 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%