通过热压缩试验研究了具有初始片层组织的TC17钛合金在780~860℃和应变速率0.001~10 s-1范围内的热变形行为和组织演变.分析了该合金在两相区变形的应力-应变曲线特征,其流变应力本构关系可以用双曲正弦方程和Zener-Hollomon参数描述,得到TC17合金在两相区变形的平均激活能为488.86 kJ·mol-1.显微组织分析发现:TC17合金在两相区变形时组织演变的主要特征是片层组织球化;热变形参数严重影响片层组织球化过程的进行,加大变形量、降低应变速率以及提高变形温度可以提高片状组织的动态球化程度.
参考文献
[1] | Boyer Rodney;Welsch Gerhard;Collings E W.Materials Properties Handbook:Titanium Alloys[M].Ohio:ASM,1994 |
[2] | Wang K X;Zeng W D;Zhao Y Q.Flow behavior and microstructural evolution of Ti-17 alloy with lamellar microstructure during hot deformation in α + β phase field[J].Materials Science and Technology |
[3] | Semiatin SL;Weiss I;Seetharaman V .Flow behavior and globularization kinetics during hot working of Ti-6Al-4V with a colony alpha microstructure[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(2):257-271. |
[4] | R.M.Miller;T.R.Bieler;S.L.Semiatin .FLOW SOFTENING DURING HOT WORKING OF Ti-6Al-4V WITH A LAMELLAR COLONY MICROSTRUCTURE[J].Scripta materialia,1999(12):1387-1393. |
[5] | Pu ZJ.;Zou D.;Wu KH. .DEVELOPMENT OF CONSTITUTIVE RELATIONSHIPS FOR THE HOT DEFORMATION OF BORON MICROALLOYING TIAL-CR-V ALLOYS[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(0):780-787. |
[6] | Henshall G A;Miller A K .The influence of solutes on flow stress plateaus,with emphasis on back stresses and the development of unified constitutive equations[J].Acta Materialia,1989,37(10):2693-2704. |
[7] | Seshacharyulu T;Medeiros S C;Frazier W G et al.Microstructural mechanisms during hot working of commercial grade Ti-6A1-4V with lamellar starting structure[J].Materials Science and Engineering,2002,325:112-115. |
[8] | 王凯旋,曾卫东,赵永庆,邵一涛,周建华,王晓英,周义刚.钛合金片层α相在热加工过程中演变规律的定量研究[J].稀有金属材料与工程,2010(04):565-569. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%