在环境作用下沥青易产生静态硬化和氧化硬化,使沥青的流变特性发生改变,而严重影响沥青路面的耐久性,如何合理评价和选择沥青对确保路面使用品质至关重要.通过三种不同基质沥青的组分分析和不同老化状态下沥青的常规试验(针入度、软化点和延度试验)、SHRP试验(DSR(Dynamic Shear Rheometer)和BBR(Bending Beam Rheometer)试验)结果比较,结合FTIR(Fourier transform infrared)试验结果,分析了不同老化状态下基质沥青的老化特性和机理.结果表明,常规试验可用来描述基质沥青老化前后性能变化,但它只能提供特定温度荷载频率下的试验信息,而SHRP试验可反映沥青老化对沥青流变行为的影响,建议采用SHRP流变学指标特别是BBR试验结果评价沥青的老化特性.
参考文献
| [1] | Page G C;Murrphy K H;Ruth B E .Asphalt binder hardening--cause and effects[J].Proceeding of the Association of Asphalt Paving Technologists,1985,54:140-167. |
| [2] | Raymond E Robertson .Chemical properties of asphalts and relationship to pavement performance.[SHRP-A/UWP-91-510,][R].Strategic Highway Research Program National Research Council Washington,DC,1991. |
| [3] | D A Sosnovske;Y Abwahab;C A Bell .Role of asphalt and aggregate in the aging of bituminous mixtures[J].Transportation Research Record,1992,1386:10-21. |
| [4] | State of California Business,Transportation and Housing Agency .Method for determining asphalt durability using the California tilt-oven durability test.[California Test 374,][R].,2000. |
| [5] | C A Bell;Y AbWahab;M E Cristi;D Sosnovske .Selection of laboratory aging procedures for asphalt-aggregate mixtures.[SHRP-A-383,][R].Strategic Highway Research Program National Research Council Washington,DC,1994. |
| [6] | 魏建明,孙彦,庞伟伟,张永和,张玉贞.两种道路沥青抗老化性的表征[J].石油化工高等学校学报,2006(02):38-40,46. |
| [7] | 张争奇,梁晓莉,李平.沥青老化性能评价方法[J].交通运输工程学报,2005(01):1-5. |
| [8] | 汪东杰,葛折圣,黄晓明,田志强.沥青抗老化指标探讨[J].公路交通科技,2003(03):15-18. |
| [9] | 欧阳春发,李永胜,贾润萍,张琢,王霞,杨俊和,张隐西,王仕峰.基质沥青及聚合物改性沥青的老化研究进展[J].合成材料老化与应用,2007(02):22-28. |
| [10] | 陈华鑫,王秉纲.SBS改性沥青的动态力学性能[J].华南理工大学学报（自然科学版）,2007(07):37-40,51. |
| [11] | 王仕峰,张玉军,王迪珍,罗东山.SBS改性沥青的老化行为[J].合成橡胶工业,2003(05):301-304. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%