以一步模压工艺,采取化学交联法发泡聚丙烯(PP),研究了发泡过程中工艺条件、配方对最终产物结构和性能的影响.获得了性能较优异的发泡聚丙烯的发泡工艺条件及配方:上下横板温度180℃-190℃,模压压力7.5MPa-10.0MPa;发泡剂AC用量1.0%-1.5%,交联剂DCP用量0.1%-0.3%,成核剂SiO2用量0.15%-0.25%.
参考文献
| [1] | Reichelt;Nobert .Strategeis for achieving ultra low density polypropylene foam[J].Polymer Engineering and Science,2002,42(07):1481-1492. |
| [2] | 陈国华;彭玉成.国外微孔塑料物理发泡研究现状[J].中国塑料,1998(12):1. |
| [3] | Christopher K,Gehlsen .Foam and method[P].USA:27563,2003-11-13. |
| [4] | Naguib HE.;Park CB.;Reichelt N. .Fundamental foaming mechanisms governing the volume expansion of extruded polypropylene foams[J].Journal of Applied Polymer Science,2004(4):2661-2668. |
| [5] | 张平,周南桥,卜宪华.聚丙烯发泡成型的改性方法及发展概况[J].塑料,2006(03):34-39. |
| [6] | 段予中;徐凌秀.塑料配方设计900例[M].北京:中国石化出版社,1998:78-79. |
| [7] | 马世鹏 .聚丙烯的化学交联及应用[J].塑料加工,1998,26:8-12. |
| [8] | Zhi-Mei Xu;Xiu-Lei Jiang;Tao Liu;Guo-Hua Hu;Ling Zhao;Zhong-Nan Zhu;Wei-Kang Yuan .Foaming of polypropylene with supercritical carbon dioxide[J].The Journal of Supercritical Fluids,2007(2):299-310. |
| [9] | 山下晋三;纪奎江.交联剂手册[M].北京:化学工业出版社,1990:75-89. |
| [10] | 何亚东;信春玲 .非交联聚丙烯发泡材料的生产方法[P].中国专利.1861368,2006-6-9. |
| [11] | 大卫;伊夫斯;周南桥;彭响方.泡沫塑料手册[M].北京:化学工业出版社,2006:168-118. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%