分别研究了在湿热老化、加速湿热老化、紫外辐照老化模式下,背板的力学性能和聚酰胺熔融焓及黄度指数的变化,分析了老化前后背板的断面形貌和表面形貌变化.结果表明:湿热老化和加速湿热老化聚酰胺趋于结晶以及聚酰胺和玻璃纤维界面作用减弱；紫外辐射老化主要导致酰胺键断开,分子结构破坏.通过比较老化前后力学性能、黄度指数及表面形貌发现,紫外辐照老化对聚酰胺背板的影响较大.
参考文献
| [1] | C. R. Osterwald;T. J. McMahon .History of Accelerated and Qualification Testing of Terrestrial Photovoltaic Modules: A Literature Review[J].Progress in photovoltaics,2009(1):11-33. |
| [2] | IEC 61215:Crystalline silicon terrestrial photovoltaic (PV) modules-Design qualification and type approval[S].,2005. |
| [3] | IEC 61730:Photovoltaic (PV) module safety qualification-Part 1:Requirements for construction,Part 2:Requirements for testing[S].,2004. |
| [4] | IEC 61646:Thin-film terrestrial photovoltaic modules-design qualification and type approval[S].,2007. |
| [5] | G. Oreski;G.M. Wallner .Aging mechanisms of polymeric films for PV encapsulation[J].Solar Energy,2005(6):612-617. |
| [6] | 唐景,彭丽霞,张增明,傅冬华.不同老化模式对光伏背板中PET结晶度的影响[J].合成材料老化与应用,2011(02):40-46. |
| [7] | Zhiyong xia;John H Wohlgemuth;Dqniel W Cunningham.A Lifetime Prediction of PV Encapsulant and Backsheet Via Time Temperature Superposition Principle[A]. |
| [8] | 李兰艳,李光吉,李超,王志.尼龙6在热氧老化中的性能与结构变化[J].塑料科技,2009(12):36-41. |
| [9] | Agnes Roger;Daniel Sallet;Jacques Lemaire .Photochemistry of aliphatic polyamides.4.Mechanisms of photooxidation of polyamides6,11 and 12 at long wavelengths[J].Macromolecules,1986,19(03):579-584. |
| [10] | Jacques Lemaire;Jean-Lue Gardette;Agnès Rivaton;Agnès Roger .Dual Photo-chemistries in Aliphatic Polyamides,Bisphenol A Polyearbonate and Aromatic Polyurethanes-A Short Review *[J].Polymer Degradation and Stability,1986,15:1-13. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%