针对碳纤维具有疏水性难以在其表面上直接镀铜的特点,研究了碳纤维的表面改性处理,研究了影响化学镀铜溶液稳定性的因素.结果表明:采用高温灼烧除胶和过硫酸铵氧化,较好地改善了碳纤维的疏水性,提高了碳纤维表面的粗糙度;同时采用双络合体系,加入适量的2,2′-联吡啶、亚铁氰化钾,提高了镀液稳定性,碳纤维表面镀层光亮、均匀、致密,具有较好的结合力.
参考文献
| [1] | 吴利英,高建军,靳武刚.金属基复合材料的发展及应用[J].化工新型材料,2002(10):32-35. |
| [2] | JU C P;Chen K I;Lin J H .Process,microstructure and properties of squeeze-castshort-carbon-fibre reinforced aluminiummatrix composites[J].Journal of Materials Science,1994,29:5127-34. |
| [3] | Victor C Li;Karthikeyan Hobla .Effect of fiber cement composites[J].Composites Engineering,1994,4(09):947-964. |
| [4] | Milan Paunovic .Properties and structure of electroless copper[J].Plating and Surface Finishing,1985,75(02):52-54. |
| [5] | Wei-Tsu Tseng;Chia-Hsien Lo;Shih-Chin Lee .Electroless Deposition of Cu Thin Films with CuCl_2-HNO_3 Based Chemistry[J].Journal of the Electrochemical Society,2001(5):C327-C332. |
| [6] | Honama H;Kobayashi .Electroless copper deposition presence using glyoxylic acid as a reducing agent[J].Journal of the Electrochemical Society,1994,141(03):730-733. |
| [7] | 何为,唐先忠,迟兰州.碳纤维表面化学镀镍工艺研究[J].电镀与涂饰,2003(01):8-11. |
| [8] | Francis J Nuzzi .Accelerating the rate of electroless copper plating[J].Plating and Surface Finishing,1998,73(01):52-54. |
| [9] | 钟丽萍,赵转青,黄逢春.化学镀铜溶液稳定性和沉铜速率的研究[J].材料保护,2001(06):26-27. |
| [10] | 庹新林,王伯羲.碳纤维表面镀铜的研究[J].北京理工大学学报,1999(05):642-645. |
| [11] | 王济国.碳纤维表面的化学镀铜[J].新型碳材料,1996(04):44-48. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%