研究了CaO的添加量和烧结温度对10NiO-NiFe2O4复合陶瓷的物相组成、致密度和导电性能的影响.结果表明:0%～4% (质量比,下同)CaO含量范围内,烧结样品的XRD图谱仅有NiO和NiFe2O4的衍射峰.CaO掺杂对10NiO-NiFe2O4复合陶瓷具有明显的助烧作用.材料在烧结温度为1 200 ℃,CaO掺杂量为2%时,致密度达到最大为98.75%,比相同温度下未掺杂CaO的样品提高20%左右.CaO掺杂量对1 200℃烧结的10NiO-NiFe2O4复合陶瓷的电导率影响显著.当CaO掺杂量为0%～1%时,材料电导率在500～650℃区间出现1～2个数量级的突降;当CaO质量分数为2%和4%时,材料电导率在30～960℃范围内随着测试温度的升高而增大;其中,添加2%CaO样品的电导率在960℃下可达到最大为16.29 S/cm.
参考文献
| [1] | Gray P T.Corrosion and passivation of cermet inert anodes in cryolite-type electrolytes[A].Warrendale,Pa:TMS,1986:309-320. |
| [2] | 刘业翔.铝电解惰性阳极与可湿润性阴极的研究与开发进展[J].轻金属,2001(05):26-29. |
| [3] | Pawlek R P.Inert anodes:an update[A].Warrendale,Pa:TMS,2002:449-456. |
| [4] | H. XIAO;R. HOVLAND .Studies on the Corrosion and the Behavior of Inert Anodes in Aluminum Electrolysis[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1996(2):185-193. |
| [5] | Ghosh A;Das S K;Biswas J R et al.The effect of ZnO addition on the densification and properties of magnesium aluminum spinel[J].Ceramics International,2000,26(06):605-608. |
| [6] | Sarkar Ritwik;Das Samir Kumar;Banerjee Goutam .Effect of addition of Cr2O3 on the properties of reaction sintered MgO-Al2O3 spinels[J].Journal of the European Ceramic Society,2002,22(08):1243-1250. |
| [7] | 焦万丽,张磊,姚广春,刘宜汉.NiFe2O4及添加TiO2的尖晶石的烧结过程[J].硅酸盐学报,2004(09):1150-1153. |
| [8] | 席锦会,刘宜汉,姚广春.MnO2对镍铁尖晶石惰性阳极材料性能的影响[J].功能材料,2005(03):374-376. |
| [9] | 赖延清,张刚,李劼,刘业翔.金属含量对Cu-Ni-NiFe2O4金属陶瓷导电性能的影响[J].中南大学学报（自然科学版）,2004(06):880-884. |
| [10] | 关振铎;张中太;焦金生.无机材料物理性能[M].北京:清华大学出版社,2002:212-213. |
| [11] | Junzo T;Toyohiko I.Effect of additives on magnetization of ferrites[A].Tokyo:D Reidel publishing company,1980:178-181. |
| [12] | 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1997:272-280. |
| [13] | 施剑林 .高性能陶瓷与先进陶瓷固相烧结理论研究进展[J].世界科技研究与发展,1998,20(05):124-128. |
| [14] | 张刚,李劼,赖延清,孙小刚.烧结气氛对Ni-Fe尖晶石陶瓷致密化和导电性能的研究[J].功能材料,2005(11):1709-1711. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%