无铬达克罗是通过无铬钝化技术在金属材料表面形成的耐腐蚀性能佳、环境污染小、对人体健康几乎没有危害的金属表面防护膜层.本文综述了国内外形成这种膜层的物质的研究进展,展望了无铬钝化技术的发展趋势；在总结与分析的基础上指出:随着环境保护要求的提高,有机聚合物(硅烷或树脂)和稀土盐(铈盐)组成的复合成膜体系有着较好的开发和应用前景.
参考文献
| [1] | Yasuhiko Endo;Tomio Sakai;Saburo Shimada .Surface coated aluminum fine powder and aqueous chromium-free corrosion inhibiting coating composition including the same[P].United States Patent,6740424,2004. |
| [2] | 徐军明 .锌铬化学转化膜的制备、性能和结构研究[D].燕山大学,2000. |
| [3] | 胡会利 .无铬锌铝烧结涂料的研制及耐蚀机理[D].哈尔滨工业大学,2008. |
| [4] | 于升学,陈玲,李宁.烧结式锌铝涂层的粘结原理研究[J].电镀与环保,2001(05):20-21. |
| [5] | 韩树民,郑炀曾,于升学,徐军明.锌铝铬膜的防腐性能与机理[J].中国有色金属学报,2002(03):619-623. |
| [6] | Prosek T;Thierry D .Mobility and mode of inhibition of chromate at defected area of organic coatings under atmospheric conditions[J].Corrosion,2004,60(12):1122-1132. |
| [7] | Meyer U;Atrens A .Influence of environmental cariables on erosion-corrosion of carbon steel in spent liquor reheaters in bayer plant[J].Wear,1995,189(03):107-116. |
| [8] | 江澜,王小兰.铬的生物作用及污染治理[J].重庆工商大学学报(自然科学版),2004(04):325-328. |
| [9] | 张义贤,李向科.Cr6+污染致大麦幼苗基因组DNA损伤效应的研究[J].农业环境科学学报,2008(02):430-434. |
| [10] | 张俊敏,张宏,文自伟,王永琪.达克罗技术的现状与发展方向[J].表面技术,2004(06):11-12. |
| [11] | 张伟明.交美特--取代达克罗的表面处理新技术[J].材料保护,2003(04):15-16. |
| [12] | 于元春,李宁,胡会利,张景双,屠振密.无铬钝化与三价铬钝化的研究进展[J].表面技术,2005(05):6-9. |
| [13] | 黄华清 .非电解性金属防腐涂料[P].中国,01113418.6,2001-11-28. |
| [14] | 刘鸿康;贺子凯;王敏 等.低铬型锌铬涂料[P].中国,200310110774.1,2004-09-15. |
| [15] | 于兴文,李自松,曹楚南.锌铬膜工艺的初步研究[J].电镀与精饰,2001(02):5-8. |
| [16] | 何建波,鲁道荣,何百林,李学良.含硼片状锌热固涂层耐蚀性与结构的研究[J].化学研究与应用,2002(01):48-50,封3. |
| [17] | 郝建军,安成强,邵忠财,常丽丽,刘常升.A3钢镀锌层钼酸盐钝化膜的组成和性能[J].材料研究学报,2006(04):427-430. |
| [18] | Konno H;Narumi K;Habazaki H.Molybdate/A1 (Ⅲ)composite films on steel and zinc-plated steel by chemical conversion[J].Corrosion Science,2002(44):1889-1900. |
| [19] | Vukassovich M S;Farr J P G .Molybdate in corrosion inhibition-A review[J].Materials Performance,1986,25(05):9. |
| [20] | 吴伟峰 .非电解性会属防腐涂料[P].CN,1539890,2004. |
| [21] | 赵全玺 .无机磷酸盐涂料[P].CN,1232060,1999. |
| [22] | 朱筱军,何明奕,刘丽,王胜民.水性铝基金属微粉涂层的性能研究[J].电镀与涂饰,2006(01):27-29. |
| [23] | 张树永;康彪;张桃 .一种无铬达克罗涂料[P].CN,101260252,2008. |
| [24] | 鲁俊,梁英,汤尚文,甘舟,樊庆春.无铬达克罗涂料工艺及耐蚀性能研究[J].应用化工,2011(04):612-613,617. |
| [25] | 周渝生.无铬钝化技术研究的进展[J].钢铁,2003(04):68-71. |
| [26] | 姜丹 .水性无铬锌铝涂层的制备与性能研究[D].昆明:昆明理工大学,2009. |
| [27] | Danqing Zhu;Wim J;Van Ooij.Corrosion protection of metals by water - based silanemixtures of bis -[trimethoxysilylpropyl]amine and vinyltriacetoxysilane[J].Progress in Organic Coatings,2004(49):42-53. |
| [28] | 胡吉明,刘倞,张鉴清,曹楚南.LY12铝合金表面电化学沉积制备DTMS硅烷膜及其耐蚀性研究[J].高等学校化学学报,2006(06):1121-1125. |
| [29] | Montemor M.F.;Simoes A.M. .The corrosion performance of organosilane based pre-treatments for coatings on galvanised steel[J].Progress in Organic Coatings: An International Review Journal,2000(1):17-26. |
| [30] | Guhde,Donald,Dorsett et al.Water-reducible coating composition for providing corrosion protection[P].US,5868819,1999-08-02. |
| [31] | 李宁;胡会利;黎德育 .烧结式金属粉末涂料及以其制备金属陶瓷防腐涂层的方法[P].CN,1597617,2005-03-23. |
| [32] | 周文娟,许立坤,王佳,李宁,薛丽莉,陈光章.碳钢表面硅烷锌铝涂层的腐蚀电化学行为[J].金属学报,2007(09):983-988. |
| [33] | 汪庆年 .无铬金属防腐涂料、制备方法及使用方法[P].CN,101338091,2009-01-07. |
| [34] | 陈鹏,王旭东,孙冬柏,孟惠民,俞宏英,樊自拴.环保型锌铝基耐蚀涂层的制备与性能[J].机械工程材料,2010(02):67-70. |
| [35] | Ferreira M G S;Duarte R G;Montemor M F.Silanes and rare earth salts as chromate replacers for pre-treatments on galvanized steel[J].Electrochimica Acta,2004(49):2927-2935. |
| [36] | 卢锦堂,张双红,孔纲,车淳山.镀锌钢上钼酸盐/硅烷复合膜的组成与耐蚀性[J].华南理工大学学报（自然科学版）,2009(12):12-17. |
| [37] | 马蒂亚斯·科赫;科斯廷·莫茨凯特;卡斯滕·哈克巴斯 等.不含铬的防腐剂和防腐蚀方法[P].中国,00807712.6,2002-06-05. |
| [38] | 周文娟 .水性锌铝粉防腐涂层的研究[D].中国海洋大学,2007. |
| [39] | 王典,刘建国,殷跃军,韩长智,严川伟.钛添加剂对无铬达克罗防护性能的影响[J].腐蚀科学与防护技术,2009(04):426-428. |
| [40] | 石存秀,曾鹏,李国亮,谢光荣.稀土盐对水性锌铝合金涂层的微观结构与耐蚀性能的影响[J].电镀与涂饰,2010(06):51-54. |
| [41] | 季利亚,姚正军.无铬达克罗涂层的工艺研究[J].电镀与环保,2011(03):22-24. |
| [42] | Wei-Gang Ji;Ji-Ming Hu;Jian-Qing Zhang;Chu-Nan Cao .Reducing the water absorption in epoxy coatings by silane monomer incorporation[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(11):3731-3739. |
| [43] | 黄琪,张佐光,王善琦.耐热强韧性环氧树脂基体的性能[J].高分子材料科学与工程,2008(04):78-81. |
| [44] | 孟中;徐关庆 .镁合金无铬达克罗溶液涂料及其生产方法[P].CN,1786091,2006-06-14. |
| [45] | 刘建国;于典;殷跃军 .一种水性防腐涂料及其制备方法[P].CN,101041760,2007-09-26. |
| [46] | 王再德,陈玲,焦明泉,李潇,周杨,佟琦.无铬达克罗工艺的研究[J].电镀与环保,2008(05):34-35. |
| [47] | 江曼,毕渭滨,毛钢红,万丽娟,郑茂盛.新型无铬达克罗防腐材料[J].西北大学学报（自然科学版）,2010(02):215-218. |
| [48] | 乔维,蔡晓兰,李明明,王开军.采用硅烷黏结剂制备无铬锌铝涂层[J].电镀与涂饰,2010(12):61-63. |
| [49] | 刘立炳,刘晔红.无铬锌铝膜层的开发与在铝合金阀体件上的应用[J].电镀与精饰,2011(02):13-14,18. |
| [50] | 王全全 .新型防腐涂层无铬达克罗的制备及耐蚀机理研究[D].武汉科技大学,2010. |
| [51] | Clermont F R;Creil F R;Saint Witz F R et al.Use of MoO3 as corrosion inhibitor, and coating composition containing such an inhibitor[P].US,416375,2004-07-22. |
| [52] | 高节明 .无铬达克罗涂液的制备与性能研究[D].昆明:昆明理工大学,2007. |
| [53] | 张巧云.低碳钢表面锌-铝复合涂层的研究[J].表面技术,2011(01):53-55. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%