利用超声分散法对团聚的原始碳纳米管分散处理后,通过酸化、敏化、活化等步骤对其进行表面改性处理,采用表面化学镀在其表面镀覆镍层,并进行热处理.研究了碳纳米管的分散、表面改性和镀镍工艺对镀层质量的影响.实验结果表明:在乙醇溶液中,利用分散剂进行超声分散可以明显改善碳纳米管之间的团聚状况;经过酸化、敏化、活化处理后其表面可形成密集的活化点;镀镍温度在20℃左右,pH值约8.2时,所得镀层较为均匀,经410℃保温2h的热处理后,镀层变得光滑、连续、致密,镀层的厚度为12~20nm.
参考文献
[1] | 陈小华,王健雄,邓福铭,李宏健,王淼,卢筱楠,彭景翠,李文铸.碳纳米管的化学镀镍研究[J].新型炭材料,2000(04):39-43. |
[2] | Gao GH.;Goddard WA.;Cagin T. .Energetics, structure, mechanical and vibrational properties of single-walled carbon nanotubes[J].Nanotechnology,1998(3):184-191. |
[3] | Ajayan PM;Iijime S .Capillarity-induced filing of carbon nanotubes[J].Nature,1993,361:333-334. |
[4] | Satishkumar BC;Govindaraj A;Erasmus M .Oxide nanotubes preperaed using carbon nanotubes as templating[J].Materials Research,1997,12:604-607. |
[5] | 李维学,金辉,戴剑锋,王青,徐莺歌.镀镍单壁碳纳米管镁基复合材料的微观组织研究[J].甘肃科学学报,2010(03):80-83. |
[6] | 郭忠诚;杨万显.化学镀镍原理及应用[M].昆明:云南科学技术出版社,1998 |
[7] | Zhang Y;Franklin Nathan W;Chen Robert J et al.Metal coating on suspended carbon nanotubes and its implication metal-tube interaction[J].Chemical Physics Letters,2000,331:35-41. |
[8] | Zhang YJ.;Li YB.;Wang NL.;Zhu J.;Zhang Q. .Coating of carbon nanotubes with tungsten by physical vapor deposition[J].Solid State Communications,2000(1):51-55. |
[9] | 杨建华.强束流脉冲金属离子束表面改性技术及其应用[J].表面技术,2003(01):59-61. |
[10] | 李静,孙晓刚,曹素芝.碳纳米管表面化学镀Ni的研究[J].材料导报,2007(07):153-155. |
[11] | Ebbesen T W;Hjura H;Mar gare E .Carbon nanotubes decoration[J].Advanced Materials,1996,8:155-156. |
[12] | Ajayan PM;Liiima S .Capillarity induced filling of carbon nanotubes[J].Nature,1993,361:333. |
[13] | 陈小华,陈传盛,孙磊,李文华,杨植,许龙山.碳纳米管的表面修饰及其在水中的分散性能研究[J].湖南大学学报(自然科学版),2004(05):18-21. |
[14] | 李博,廉永福,施祖进,顾镇南.单层碳纳米管的化学修饰[J].高等学校化学学报,2000(11):1633-1635. |
[15] | 易国军,陈小华,蒋文忠,张刚,陈传盛.碳纳米管的表面改性与镍的包覆[J].中国有色金属学报,2004(03):479-483. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%