采用原位反应烧结工艺制备了ZrO2增韧莫来石(ZTM)复相陶瓷.研究和分析了在Y2O3为2mol%的情况下,CeO2添加量(用2Y2O3-xCeO2)对ZTM复相陶瓷相组成,显微结构及力学性能的影响.结果表明,当CeO2添加量大于4.5mol%时,CeO2同ZrO2固溶,形成相对的t-ZrO2;当CeO2添加量在1.5～4.5mol%时,ZrO2晶格畸变,晶胞长大,缺陷增加,CeO2偏析、聚集,力学性能下降.当CeO2添加量为6.5mol%时,ZTM复相陶瓷的抗弯强度达到370Mpa,断裂韧性为4.8Mpa*m1/2.
参考文献
| [1] | Nils Claussen;Jurgen Juhn .[J].Journal of the American Ceramic Society,1980,63(03):228. |
| [2] | Qi-ming Yuan;Jia qi tan;Guo-jin Zhang .[J].Journal of the American Ceramic Society,1986,69(03):265. |
| [3] | J S Moya;M L Osendi.[J].Journal of Materials Science,1984(19):2909. |
| [4] | F Camier;C Bandin.Dela Latra[J].British Ceramic Transactions,1984(83):196. |
| [5] | 李世普.特种陶瓷工艺学[M].武汉:武汉工业大学出版社,1990 |
| [6] | 李健君 等.[J].硅酸盐学报,1996,24(03):342. |
| [7] | 贺振富.[J].硅酸盐通报,1996(05):28. |
| [8] | R Mcpherson .[J].Journal of the American Ceramic Society,1986,69(03):297. |
| [9] | E Dirupo;M R Anseace.[J].Journal of Materials Science,1980(15):114. |
| [10] | N Kapuri;K N Rai;G S Upadhyaya.[J].Ceramic Industries International,1995(12):312. |
| [11] | 梁开明;顾扣芬 等.[J].硅酸盐学报,1995,25(05):477. |
| [12] | Koji Tsukuma;Masahiko Shimada.[J].Journal of Materials Science,1985(20):1178. |
| [13] | Rachem Chain .[J].Journal of the American Ceramic Society,1992,73(03):694. |
| [14] | John R Hellmann;Vladimir S Stubican .[J].Journal of the American Ceramic Society,1983,64(04):226. |
| [15] | J G Duh;J U Wan.[J].Journal of Materials Science,1992(27):6197. |
| [16] | 盛绪敏 等.[J].硅酸盐学报,1988,16(01):1. |
| [17] | 杜海清;李玉书.工业陶瓷[M].长沙:湖南大学出版社,1989 |
| [18] | 刘维跃.[J].硅酸盐通报,1996(03):10. |
| [19] | 黄勇 等.[J].硅酸盐学报,1996,18(03):10. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%