对溶胶-凝胶法进行改性,使凝胶聚沉为沉淀物,进而可以成功地合成ZrO2(9mol% Y2O3)纳米粉体.采用热重-差热(TG-DTA)分析、粒度分布分析(CILAS)、透射电子显微镜(TEM)和X射线衍射(XRD)测试对粉料制备工艺过程进行了研究.结果表明,改性的溶胶-凝胶法,在聚沉前加入分子量大小不同的表活剂,聚沉后采用无水乙醇超声分散,可以有效地消除团聚现象.沉淀产物在450℃以下可以完全分解为ZrO2(Y2O3)粉体,600℃煅烧颗粒粒度为14nm.
参考文献
| [1] | Hetrick R E;Schamp A L .Capacitive air-fuel ration sensor[J].Sensors and Actuators,1994,B21:5-10. |
| [2] | Robertson N L;Michaels N .Oxygen Exchange on Platinum in Zirconia Cell:Location of Electrochemical Reaction Sites[J].Journal of the Electrochemical Society,1990,137:129-135. |
| [3] | 简家文,杨邦朝,张益康.汽车用氧传感器的工作原理及其应用[J].传感器技术,2002(03):55-57. |
| [4] | Brune A.;Fisler D.;Wagner JB.;Lajavardi M. .The electrical conductivity of yttria-stabilized zirconia prepared by precipitation from inorganic aqueous solutions[J].Solid state ionics,1998(1/2):89-101. |
| [5] | Vladimir V;Sridic;Radovan P;Omorjan .Electrical conductivity of sol-gel derived yttria-stabilized zirconia[J].Ceramics International,2001,27(08):859-863. |
| [6] | Takayuki Tsukada;Sridhar Venigalla;Augusto A. Morrone;James H. Adair .Low-temperature hydrothermal synthesis of yttrium-doped zirconia powders[J].Journal of the American Ceramic Society,1999(5):1169-1174. |
| [7] | 陈大明;孟国文 等.ZrO2基纳米超微粉生产技术与粉体特性[J].粉体技术,1996,2(02):7-2. |
| [8] | Li W;Gao L;Guo J K .Synthesis of yttria-stabilized zirconiananoparticles by heating of alcohol-aqueous salt solutions[J].Nano-Structured Materials,1998,10(06):1043-1049. |
| [9] | 李懋强 .乳液法制备氧化锆粉体的研究[J].粉体技术,1995,1(03):11-15. |
| [10] | 牛新书,王新军.乳化分散法合成ZrO2纳米晶[J].化学研究与应用,2000(03):269-272. |
| [11] | 杨刚,罗军明,袁永瑞,张强,张海宝.共沉淀法制备ZrO2超细复合粉过程中团聚现象的研究[J].南昌航空工业学院学报(自然科学版),2001(02):15-17,26. |
| [12] | 黄浪欢,曾令可,罗民华.湿化学方法制备纳米粉体时团聚现象的探讨[J].佛山陶瓷,2001(10):11-13. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%