等离子喷涂Fe基非晶合金涂层的晶化温度在590℃左右.在高于晶化温度热处理时,涂层首先以多晶型晶化方式直接结晶形成亚稳的Fe23(c,B)6和Fe23B6化合物相.随热处理时间延长,Fe23(C,B)6和Fe23B6相发生分解,逐渐转变为更稳定的Fe3B相和Fe固溶体相.热处理温度越高,Fe23(C,B)6相和Fe23B6相的分解转变速度越快.随热处理温度升高或时间的延长,晶化涂层的硬度呈线性降低.经590℃,4h热处理后,涂层结晶形成纳米晶组织;经660℃,4h热处理后,涂层结晶形成树枝状晶组织,随热处理温度升高,涂层中扁平状粒子间结合增强并趋于熔合,晶粒发生长大.
参考文献
| [1] | 王一禾;杨膺善.非晶态合金[M].北京:冶金工业出版社,1989 |
| [2] | K Kishitake .Thermal sprayed Fe-10Cr-13P-7C amorphous coatings possessing excellent corrosion resistance[J].Journal of Thermal Spray Technology,1996,5(04):476. |
| [3] | 周飞;卢柯 .非晶态合金条带高压复合法制备大块非晶态合金[J].材料研究学报,1997,11(02):127. |
| [4] | 钟敏霖;刘文今 .Fe-Cr-Si-B合金连续激光非晶化及非晶形成条件的研究[J].金属学报,1998,34(04):413. |
| [5] | Wu Xiaolei;Hong,Youshi .F-based thick amorphous-alloy coating by laser cladding[J].Surface and Coatings Technology,2001,141(2-3):141-144. |
| [6] | Dent AH.;McCartney DG.;Harris SJ.;Horlock AJ. .Microstructural characterisation of a Ni-Cr-B-C based alloy coating produced by high velocity oxy-fuel thermal spraying[J].Surface & Coatings Technology,2001(2/3):244-250. |
| [7] | Kishitake K;Era H;Otsubo F .Characterization of plasma sprayed Fe-17 Cr-38Mo-4C amorphous coatings crystallizing at extremely high temperature[J].Journal of Thermal Spray Technology,1996,5(03):283-288. |
| [8] | 向兴华,刘下义,朱晖朝.Fe基非晶合金涂层的等离子喷涂制备工艺研究[J].材料工程,2002(02):10-12,插2. |
| [9] | 穆晓冬,向兴华,刘正义.Fe基非晶合金涂层在晶化过程中的硬度与组织变化[J].材料工程,2003(05):33-36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%